Abstract:Hybrid plasma spraying combines plasma spraying of dry coarse powders and liquids (suspensions or solutions) potentially providing high deposition rates and coatings with novel microstructures and amended functionality. Such composites may be potentially interesting also for the thermal barrier coatings (TBCs). In this study, the first experimental TBCs with hybrid ceramic top-coats were deposited by hybrid water-/argon-stabilized plasma (WSP-H) technology. Coarse dry YSZ (yttria-stabilized zirconia: ZrO 2 -Y 2 O 3 ) powder was selected to form the top-coat matrix. Suspensions of YSZ, Al 2 O 3 (alumina), YAG (yttrium aluminum garnet: Y 3 Al 5 O 12 ), or GZO (gadolinium zirconate: Gd 2 Zr 2 O 7 ) were the source of the additional miniature phase. Uniform functionalized coatings with TBC-relevant thickness and microstructure were successfully deposited. Hybrid and reference coatings deposited also with WSP-H torch and with YSZ feedstocks showed comparable thermal diffusivity regardless of the spraying conditions but the addition of Al 2 O 3 and YAG increased it by ~ 65%, whereas GZO decreased it by ~ 20%. Thermal cycling resistance of the coatings was evaluated by thermal cycling fatigue (TCF) test. Hybrid coating with the addition of YSZ miniature phase endured on average 640 TCF cycles, which was 250-300 cycles less than the reference YSZ coatings deposited without liquid feedstocks but still comparable to the currently used YSZ-based industrial TBCs. Coatings with dissimilar chemistry of additional miniature splats showed inferior mean TCF lifetimes: GZO 438 cycles, Al 2 O 3 272 cycles, and YAG 173 cycles, opening space for further coating optimization. All hybrid coatings failed above the bond-coat/top-coat interface. Comparison of coatings before and after the thermal exposure by scanning electron microscopy (SEM) and x-ray diffraction (XRD) revealed possible changes within the coating microstructure, namely sintering (typical for top-coat consisting only of YSZ), conversion of metastable and amorphous phase (top-coats with the addition of Al 2 O 3 and YAG) or interaction between the matrix and secondary phase (top-coat with the addition of GZO).

Formation Mechanism of an Ultra-Low Thermal Conductivity Thermal Barrier Coating Deposited Using Biomimetic Hierarchical Porous Microspheres

Structural Optimization for the Thermal Conductivity and Thermal Cycling Behavior in Thermal Barrier Coatings and Analysis of Thermomechanical Properties by Computational Investigation

Microstructure and Thermal Properties of the Early-Stage Experimental Thermal Barrier Coatings Deposited by Hybrid Plasma Spraying

Fast synthesis of novel micron porous particles of Gd, Yb and Y-stabilized zirconia to prepare TBCs with low thermal conductivity

Effect of spraying ceramic powder pore structure on thermophysical properties of plasma-sprayed thermal barrier coatings

Microstructural Characterization and Thermal Barrier Effects of Conventional and Nanostructured Zro2-7wt.%Y2o3 Thermal Barrier Coatings Deposited by Plasma Spraying

Low Thermal Conductivity Yttrium Aluminum Garnet Thermal Barrier Coatings Made by the Solution Precursor Plasma Spray: Part I—Processing and Properties

Thermal Conductivity of Multi-Sized Porous Thermal Barrier Coatings at Micro and Nano Scales after Long-Term Service at High Temperatures

A transmission electron microscopy study of the microstructure and interface of zirconia-based thermal barrier coatings

Tailoring the thermal conductivity of Sc2O3–Yb2O3 Co-stabilized ZrO2 thermal barrier materials and mechanism insight

Study on Construction Mechanism of Ceramic–Metal Thermal Barrier Coating System by Plasma Spraying

Structure and Properties of Thermal Barrier Coating Prepared by Alumina Coated Zirconia Composite Powder

Low Thermal Conductivity Yttrium Aluminum Garnet Thermal Barrier Coatings Made by the Solution Precursor Plasma Spray: Part II—Planar Pore Formation and CMAS Resistance

Preparation and thermophysical properties of Dy2Zr2O7 ceramic for thermal barrier coatings

Rear Earth Oxide Multilayer Deposited by Plasma Spray-Physical Vapor Deposition for Envisaged Application as Thermal/Environmental Barrier Coating

Preparation and sintering behavior of GdYb-YSZ nanostructured thermal barrier coating

High‐Temperature Aging of Plasma Sprayed Quasi‐Eutectoid LaYbZr2O7–Part II: Microstructure & Thermal Conductivity

Investigating the Cmas Corrosion Resistance and Thermal Cycling Failure Behavior of Porous Thermal Barrier Coatings with Different Morphologies Prepared by Plasma Spraying

Enhanced thermal radiation blocking of plasma spraying thermal barrier coatings with a bimodal splat thickness distribution

High Temperature Thermal Properties of Columnar Yttria Stabilized Zirconia Thermal Barrier Coating Performed by Suspension Plasma Spraying

Wetting, infiltration, and interaction behavior of calcium-magnesium-alumino-silicate towards Gd/Yb-modified SrZrO3 coatings deposited by solution precursor plasma spray