Abstract:A reciprocating extrusion process was developed to consolidate 6061-Al 2 O 3 p composites from mixed powders. The 6061 alloy powder was first dehydrated in a vacuum chamber at 450 °C and then mixed with 12.5 µm Al 2 O 3 powder in various volume fractions: 0, 5, 10, 20, and 30 pct. The mixed powders were hot pressed at 300 °C under a pressure of 300 MPa and finally extruded reciprocatingly 14 times at 460 °C. The results show that the composites were fully densified, with no sign of pores or oxide layers observable in the optical microscope. The Al 2 O 3 particles were distributed uniformly in the matrix. As compared with 6061 alloys, the composites demonstrated a smaller precipitation hardening and elongation, but exhibited a higher Young’s modulus and a larger work hardening capacity. The degradation of precipitation hardening was due to the loss of Mg, which reacts with Al 2 O 3 to form MgAl 2 O 4 . The large work-hardening capacity is attributable to the incompatibility between Al 2 O 3 and the matrix, which possibly generates more dislocations to harden the matrix. The composites had much higher friction coefficients and greater wear resistances than the 6061 alloy against steel disc surface. The friction coefficient of the 6061-30 vol pct Al 2 O 3 p composite was double that of the 6061 alloy and the wear resistance was 100-fold. As compared with similar composites reported previously, these composites possessed much higher elongation at the same strength level. A 30 vol pct Al 2 O 3 p still displayed an elongation of 9.8 pct in the T6 condition. All of these improvements are attributed to the merits, including full densification of the bulk, uniform dispersion of the Al 2 O 3 particles in the matrix, and strong binding between the Al 2 O 3 particles and the matrix resulting from reciprocating extrusion.

Fabrication of Al2O3/6061 Particles Composite Materials by Pulse Squeeze Exhaust Casting.

Fabrication of Al2O3/6061 particles composite materials by pulse squeeze exhaust casting

Squeeze-Exhaust Casting of Al<sub>2</sub>O<sub>3p</sub>/6061 Composites Material with High Densification and Strength

Fabrication and Mechanical Properties of Particle Dispersed Al-Al2O3 Composite Materials.

MMCs with Controlled Non-Uniform Distribution of Submicrometre Al2O3particles in 6061 Aluminium Alloy Matrix

Fabrication of Nanocrystalline Zro2 Particle Reinforced Aluminum Alloy Composite by Squeeze Casting Route

High Strength Al(2)O(3)P/6061 Al Composites: Effect Of Particles, Subgrains And Precipitates

Tensile deformation behavior of a sub-micrometer Al2O3/6061Al composite

High Strength Al–Al2O3p Composites: Optimization of Extrusion Parameters

Al2o3 Particles Reinforced Aluminium Matrix Composite Fabricated By Pressureless Infiltration Technique

High strength Al<SUB>2</SUB>O<SUB>3p</SUB>/6061 Al composites: effect of particles, subgrains and precipitates

Fabrication and properties of in situ (Al3Zr + Al2O3)p/A356 composites cast by permanent mould and squeeze casting

The Fabrication and Properties of the Squeeze-Cast TiN/Al Composites

Microstructure and Mechanical Properties of High Strength Al2o3p/6061al Composites

Study of 6061-Al2o3p Composites Produced by Reciprocating Extrusion

Sicp/Al Composites Fabricated by Modified Squeeze Casting Technique

Microstructure and Mechanical Properties of High Strength Al<sub>2</sub>O<sub>3p</sub>/6061Al Composites

Ultrasonic Assisted Squeeze Casting of a Wrought Aluminum Alloy

Microstructure, Interface and Fabricating Process of Al_2O_3-SiO_2/AZ91D Composites Prepared by Squeeze Infiltration

Fabrication and mechanical properties of high-volume-fraction Si 3 N 4 -Al-based composites by squeeze infiltration casting

High Strength Al2O3p/2024Al Composites – Effect of Particles, Subgrains and Precipitates