Abstract:A reciprocating extrusion process was developed to consolidate 6061-Al 2 O 3 p composites from mixed powders. The 6061 alloy powder was first dehydrated in a vacuum chamber at 450 °C and then mixed with 12.5 µm Al 2 O 3 powder in various volume fractions: 0, 5, 10, 20, and 30 pct. The mixed powders were hot pressed at 300 °C under a pressure of 300 MPa and finally extruded reciprocatingly 14 times at 460 °C. The results show that the composites were fully densified, with no sign of pores or oxide layers observable in the optical microscope. The Al 2 O 3 particles were distributed uniformly in the matrix. As compared with 6061 alloys, the composites demonstrated a smaller precipitation hardening and elongation, but exhibited a higher Young’s modulus and a larger work hardening capacity. The degradation of precipitation hardening was due to the loss of Mg, which reacts with Al 2 O 3 to form MgAl 2 O 4 . The large work-hardening capacity is attributable to the incompatibility between Al 2 O 3 and the matrix, which possibly generates more dislocations to harden the matrix. The composites had much higher friction coefficients and greater wear resistances than the 6061 alloy against steel disc surface. The friction coefficient of the 6061-30 vol pct Al 2 O 3 p composite was double that of the 6061 alloy and the wear resistance was 100-fold. As compared with similar composites reported previously, these composites possessed much higher elongation at the same strength level. A 30 vol pct Al 2 O 3 p still displayed an elongation of 9.8 pct in the T6 condition. All of these improvements are attributed to the merits, including full densification of the bulk, uniform dispersion of the Al 2 O 3 particles in the matrix, and strong binding between the Al 2 O 3 particles and the matrix resulting from reciprocating extrusion.

Microstructure and Mechanical Properties of High Strength Al<sub>2</sub>O<sub>3p</sub>/6061Al Composites

Microstructure and Mechanical Properties of High Strength Al2o3p/6061al Composites

MMCs with Controlled Non-Uniform Distribution of Submicrometre Al2O3particles in 6061 Aluminium Alloy Matrix

Mechanical Properties And Microstructure Of Extruded Al2o3p/2024 Al Composites With Different Volume Fraction Reinforcement

High Strength Al(2)O(3)P/6061 Al Composites: Effect Of Particles, Subgrains And Precipitates

High strength Al<SUB>2</SUB>O<SUB>3p</SUB>/6061 Al composites: effect of particles, subgrains and precipitates

High Strength Al–Al2O3p Composites: Optimization of Extrusion Parameters

High Strength Al2O3p/2024Al Composites – Effect of Particles, Subgrains and Precipitates

Tensile deformation behavior of a sub-micrometer Al2O3/6061Al composite

High temperature compression behavior of Al2O3 particle reinforced 6061aluminum alloy composite

Study of 6061-Al2o3p Composites Produced by Reciprocating Extrusion

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF Y2O3 MODIFIED-Al2O3 PARTICLE /6061Al COMPOSITES

Microstructure and Mechanical Properties of Al/Al4C3/Al2O3 Composite

Effect of Particle Size and Morphology on Microstructure and Properties of Al2O3p/Al Composites

Effect of coating Al2O3 reinforcing particles on the interface and mechanical properties of 6061 alloy aluminium matrix composites

Microstructures and Mechanical Properties of MgAl2O4 Particle-Reinforced AC4C Aluminum Composites

Fabrication and Mechanical Properties of Particle Dispersed Al-Al2O3 Composite Materials.

Aging behavior and tensile properties of 6061Al–0.3 μm Al2O3p particle composites produced by reciprocating extrusion

Microstructures and mechanical properties ofMgAl 2

Microstructure and Mechanical Properties of Aluminum Alloy Matrix Composites Reinforced with Fe-Based Metallic Glass Particles

Microstructural Evolution and Mechanical Property of Nanoparticles Reinforced Al Matrix Composites During Accumulative Orthogonal Extrusion Process

Microstructure and Mechanical Properties of High Strength Al&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;3p&lt;/sub&gt;/6061Al Composites