Abstract:In order to overcome the serious corrosion problem of furnace hearth refractory materials for smelting reduction ironmaking, the Cr2O3–Al2O3–MgO–ZrO2 refractories were synthesized, and the phase component, microstructure, mechanical characteristics, and slag erosion behavior of composite refractories were investigated and evaluated. The results indicate that the composite refractories mainly consist of Mg(Al, Cr)2O4 spinel phase, (Al, Cr)2O3 solid solution and ZrO2. The content of Mg (Al, Cr)2O4 spinel significantly increases with the increasing MgO content, while the content of (Al, Cr)2O3 obviously decreases. Furthermore, the comprehensive mechanical properties of the MgO modified composite refractories can be obviously enhanced by increasing the MgO content, and sample S4 presents the best mechanical characteristics when the MgO addition is 10 wt%. The corresponding hardness, compressive strength and bending strength are 14.22 GPa, 267.14 MPa and 80.0 MPa, respectively. This is mainly because the formation of Mg(Al, Cr)2O4 significantly improves the densification of composite refractories, and a large number of high-strength Mg (Al, Cr)2O4 spinel “bridge” formed between the large-sized (Al, Cr)2O3 grains. The erosion test results indicate that increasing the MgO content can significantly improve the slag infiltration resistance of composite refractories, because the formation of Mg (Al, Cr)2O4 spinel layer significantly improves the densification of MgO reinforced composite refractories. Although the slag corrosion resistance of Mg(Al, Cr)2O4 is lower than that of (Al, Cr)2O3, the Cr2O3–Al2O3–MgO–ZrO2 refractories still presents good erosion resistance, permeability resistance, and excellent mechanical characteristics.

Application and Corrosion Characteristics of Chrome-Free SiC-MgAl2O4 Refractory Linings Serviced in an Entrained Flow Gasifier

Corrosion of high-chrome refractory materials by high-sodium slag in an entrained-flow gasifier

Corrosion in high alumina refractory serviced in a bench-scale entrained flow gasifier

Corrosion mechanism of Al2O3–SiC–C refractory by SiO2–MgO-based slag

Corrosion Mechanism of Alumina-Chromia Refractory by SiO2-Al2O3-CaO Based Slag from Iron Capture Process of Spent Automotive Catalyst

Improved slag corrosion resistance of MgO–C refractories with calcium magnesium aluminate aggregate and silicon carbide: Corrosion behavior and thermodynamic simulation

Improved water vapor corrosion resistance of SiC bricks via in situ formation of microporous Yb2Si2O7 bonding phase

Microstructure evolution, mechanical characteristics and erosion behavior of Cr2O3–Al2O3–MgO–ZrO2 refractories in molten reduction slag

Corrosion of MgO–C Refractory with Ladle Slags

Interactions of Cr2O3–Al2O3–ZrO2 refractory with slags in an entrained-flow coal-water slurry gasifier

Strategies to improve oxidation resistance of MgO–C refractories by decreasing oxygen potential through MgSiN2

Effect of In Situ Mg-Sialon on the Oxidation Behavior of Low-Carbon MgO-C Refractories

Corrosion behavior of CaO–Al2O3–SiO2–MgO-Cr2O3 slag on MgO refractory brick for smelting of chromite

Corrosion behavior and failure mechanism of SiC whisker and c-AlPO4 particle-modified novel tri-layer Yb2Si2O7/mullite/SiC coating in burner rig tests

Enhanced corrosion resistance of magnesia-chrome refractories impregnated with zirconia sol

Enhancement, application, and challenges of chromium–corundum high‐temperature refractories

Corrosion mechanism of cement-bonded Al2O3–MgAl2O4 pre-cast castables in contact with molten steel and slag

Corrosion mechanism of novel MgO–Al3BC3 refractories in contact with converter slag

Corrosion and Oxidation of Silicon Carbide Based on a Nitride Binder in an Aluminum Electrolyzer Side Lining

Corrosion mechanism of magnesia-chrome refractory bricks with FetO-SiO2-Cr2O3 copper converter slag

Thermal cycling behavior of bi-layer Yb2Si2O7/SiC EBC-coated Cf/SiC composites in burner rig tests