Abstract:In this paper, the influences of Cr3C2/VC content on WC grain size, WC grain shape and mechanical properties of WC–6 wt. % Co cemented carbides were investigated. The results showed that the grain size first rapidly decreased and then slightly decreased with the increasing Cr3C2/VC content, and VC led to finer grain size and narrower size distribution. HRTEM/EDS analysis of the WC/Co interface indicates that the segregation concentration of V is much larger than that of Cr, which may be a strong response to the higher inhibition efficiency of VC. The addition of Cr3C2 induced triangular prism shape WC grains while VC generated stepped triangular prism grains. Despite the grain growth inhibitor (GGI) mechanisms of Cr3C2/VC have been extensively studied in the literature, the doping amount, especially the doping limit, has not been systematically investigated. In this work, the saturated solubilities of Cr and V in cobalt binder phase along with carbon content hare been predicted based on thermodynamic calculations. Based on the theoretical calculations, the doping amount of Cr3C2/VC is designed to be gradually increasing until more or less over their maximum solubilities in the binder phase, thereby investigating the subsequent microstructure and mechanical properties. When the doping of Cr3C2/VC exceeds the maximum solubility in Co phase, Co-rich Cr-carbides and Co-deficient V-carbides would form respectively, which were detrimental to the transverse rupture strength (TRS) and impact toughness. The hardness increased with the increasing Cr3C2/VC content, while the fracture toughness decreased with the increasing Cr3C2/VC content. The TRS initially enhanced and then declined, but the stepped triangular prism shape grains and low fraction of WC/Co interface in WC–6Co–VC cemented carbide led to a more pronounced decline in the TRS. The sample with 0.6 wt. % Cr3C2 addition had good comprehensive mechanical properties, its hardness, fracture toughness and TRS were 1880 kg/mm2, 9.32 MPa·m1/2 and 3450 MPa, respectively.

Decarburization Control and Performance Enhancement: Optimizing HVOF Sprayed Submicron WC-12Co Coating with Additives

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Enhancing Comprehensive Properties of Hvof Thermally Sprayed Wc-10co Coatings Using Two Grain Inhibitors

Effects Of Wc Crystal Characteristics On Microstructure And Mechanical Property Of Hvof-Sprayed Wc-Cocr Coatings

Effect of Cobalt and Chromium Content on Microstructure and Properties of WC-Co-Cr Coatings Prepared by High-Velocity Oxy-Fuel Spraying

Effects of Submicron WC Particles Addition on Wear Performances of HVOF Sprayed WC-Co Coatings

Characterization on microstructures and properties of WC-CoCr coating deposited by HVAF and HVOF processes

Influence of WC Particle Size on the Mechanical Properties and Residual Stress of HVOF Thermally Sprayed WC–10Co–4Cr Coatings

Investigation of Novel Nano-carbide WC/CoCr Coatings Applied by HVAF

Effect of Particle and Carbide Grain Sizes on a HVOAF WC-Co-Cr Coating for the Future Application on Internal Surfaces: Microstructure and Wear

Microstructure Characterization and Abrasive Wear Performance of Hvof Sprayed Wc-Co Coatings

Effects of WC on the Microstructure, Wear and Corrosion Resistance of Laser-Deposited CoCrFeNi High Entropy Alloy Coatings

Microstructure and mechanical property of high velocity oxy-fuel sprayed WC-Cr3C2-Ni coatings

Promising WC-30WB-10Co Cemented Carbide Coating with Improved Density and Hardness Deposited by High Velocity Oxy-Fuel Spraying: Microstructure and Mechanical Properties

Microstructure and Abrasive Wear Behaviour of HVOF Sprayed Carbide-Based Cermet Coatings

Multimodal Coatings: A New Concept in Thermal Spraying

Investigation on Microstructure, Mechanical and Wear Properties of HVOF Sprayed Composite Coatings (WC-Co + CR) On Ductile Cast Iron

Preparation and Characterization of WC/Co-W-C Cermet Coatings with Molten Zinc Corrosion Resistance by HVOF Spraying of Bimodal-Structured WC/Co Powder

Thick WC-12Co Coatings on Bearing Steel Fabricated by Low-Temperature High-Velocity Fuel Spray Process

Influence of Cr3C2 and VC Content on WC Grain Size, WC Shape and Mechanical Properties of WC–6.0 wt. % Co Cemented Carbides

Wear resistance enhancement of HVOF-sprayed WC-Co coating by complete densification of starting powder