Using Pyrolytic Carbon-Coated Short Carbon Fiber to Fabricate Csf/ZrB2-SiC Composites by Direct Ink Writing and Precursor Infiltration Pyrolysis

Yixin Zhang,Yehong Cheng,Jinming Fang,Denghao Ma,Xin Sun,Junping Li,Yumin An,Chuanjin Huang,Ning Hu,Libin Zhao
DOI: https://doi.org/10.1016/j.ceramint.2024.08.211
IF: 5.532
2024-01-01
Ceramics International
Abstract:Direct ink writing (DIW) offers significant advantages for efficient manufacturing of complex ceramic composite components. However, the mechanical properties of short carbon fiber-reinforced ceramic composites fabricated by DIW technology were not ideal, mainly be ascribed to the absence of a suitable coating on the fiber as an interface. In this work, Csf/ZrB2 green bodies were printed by an optimized extrusion process using pyrolytic carbon-coated short carbon fibers (Csf). High-performance Csf/ZrB2-SiC composites were obtained through the infiltration and pyrolysis of SiC precursor six times. With increasing C sf content, the dimensional deviations decreased and the mechanical properties increased. When the C sf content was 30 vol%, the dimensional deviation of the Csf/ZrB2-SiC composite was less than-0.5 % in the X and Y directions and about-2 % in the Z direction. A marked increase in the flexural strength and fracture toughness of the composite was also obtained, reaching 275.0 MPa and 5.26 MPa m 1/2 , respectively.
What problem does this paper attempt to address?