Research on Water Resistance of Magnesium Silicon Potassium Phosphate Cement
Pengpeng Yao,Xujian Lin,Yuzhong Wu,Tao Ji,Yongning Liang
DOI: https://doi.org/10.1016/j.jobe.2024.110862
IF: 7.144
2024-01-01
Journal of Building Engineering
Abstract:Magnesium silicon potassium phosphate cement (MSPPC) is prepared by three essential components, dipotassium hydrogen phosphate (P), silica fume (SF) and dead burned magnesium oxide (M). This distinguishes MSPPC from the conventional Potassium Magnesium Phosphate Cement (MKPC), which is formulated with potassium dihydrogen phosphate (non-dipotassium hydrogen phosphate), dead burned magnesium oxide, and a retarder. The investigation delved into the impact of the P/M ratio (P/M=1/2~1/5) and silica fume content (SF=0%~20%) on the water resistance properties of MSPPC. The water resistance mechanism of MSPPC was elucidated through a comprehensive analysis of microscopic experimental results, including XRD, SEM, and pore structure analysis. Experimental results showed that with a constant silica fume content, the water resistance of MSPPC improved as the P/M ratio decreased. Specifically, when the cement paste with P/M of 1/5, W/C ratio of 0.16, and the silica fume content was 15%, the 56 d strength retention rate reached 96.03%. Reducing the quantity of dipotassium hydrogen phosphate in the system led to a decrease in the amount of unreacted phosphate, and the pore size distribution of less than 50 nm, ultimately enhancing the water resistance of MSPPC. When the P/M ratio was held constant, the water resistance of MSPPC improved as the silica fume content increased. The strength retention rate reached its maximum at a silica fume content of 20%. Specifically, the strength retention rate at 3 d, 7 d, 28 d, and 56 d were 100.31%, 99.13%, 96.54%, and 95.77%, respectively. The water stability of MSPPC is influenced by several factors, including the degree of crystallization of MgKPO4·6H2O (MKP), the types of hydration products formed, and the overall porosity of the cement. Silica fume had the ability to consume OH- in the reaction system, thereby decreasing the pH value of the alkaline environment.This, in turn, facilitates the ionization of Mg(OH)2, creating a reaction environment conducive to the formation and stability of MKP crystals. The presence of MgSiO3 and amorphous magnesium silicate phosphate compounds served to refine the pore structure within the hardened material, enhancing the compactness of MSPPC and consequently elevating its water resistance.