Abstract:The current work aimed to explore the effect of Na/Al ratios of 0.43, 0.53, 0.63, 0.73, 0.83, and 0.93, using NaOH to alter the molar ratio, on the mechanical properties of a geopolymer material, with fixing of the Si/Al molar ratio. While fixing the Na/Al molar ratio, alteration of the Si/Al ratios to 1.7, 1.75, 1.8, 1.85, 1.9, 1.95 was used, with silica fume and sodium silicate as a silica corrector. The influence on the micromorphology and macro-strength of samples was characterized through SEM, EDS, and compressive strength characterization methods. The results show that Si/Al and Na/Al molar ratios play a significant role in the microstructure and mechanical behavior of MK-based geopolymers, and revealed that the optimal molar Si/Al and Na/Al ratios for attaining maximum mechanical strength in geopolymers are 1.9 and 0.73, respectively. Under various Si/Al ratios, the macro-strength of the geopolymer mainly relies on the formation of NASH gel, rather than zeolites or silicate derivatives. The appropriate Na/Al molar ratio can contribute to the geopolymerization, but a ultra-high Na/Al molar ratio caused a high alkali state that destroyed the microstructure of the geopolymers. Regardless of the amount of water contained in the initial geopolymer raw material, the water content of Si/Al = 1.65 and Si/Al = 1.75 after curing for 10 days was almost the same, and the bound water content of the final geopolymer was maintained at about 15%. Structural water exists in geological polymer gels in the form of a chemical structure. It has effects on the structural performance strength, while free water affects the volume stability of the geological polymer. Overall, the current work provides a perspective on the elemental composition analysis, combined with the molecular structure and micromorphology, to explore the mechanical performance of geopolymers.

The Influence Mechanism of Molar Ratio on the Performance of Phosphogypsum-Modified Geopolymer Material

Study on the Mechanical Properties, Microstructure and Hydration Mechanism of Phosphogypsum-Based Geopolymer Cement with Added Micron-Sized Silica Particles

Utilizing Raw Phosphogypsum to Prepare One-Part Geopolymer: Mechanical Properties, Optimization, and Hydration Mechanisms

The Synergistic Mechanism and Stability Evaluation of Phosphogypsum and Recycled Fine Powder-Based Multi-Source Solid Waste Geopolymer

Development and optimization of phosphogypsum-based geopolymer cement

Effects of phosphogypsum on hydration properties and strength of calcium aluminate cement

Research on the Application of Phosphogypsum in Magnesium Oxysulfate Cement: A Comparison with Sand

Recycling of Waste Gypsum in Preparation of Magnesium Oxychloride Cement (MOC)

Improving the Water Resistance of Phosphoric Acid-Based Geopolymers by Optimizing the Al/Si Molar Ratio Method

Mechanical properties and soluble phosphorus solidification mechanism of a novel high amount phosphogypsum-based mortar

Enhancing Compressive Strength of Phosphogypsum-Based Geopolymer Cement with Five Alkaline Activator Combinations

Experimental investigation on the mechanical performance and microscopic characterization of desulfurization gypsum-reinforced ternary geopolymer

The effects of admixtures on the durability properties of phosphogypsum-based cementitious materials

Utilization of Phosphogypsum and Phosphate in Improving Water Resistance of Magnesium Oxychloride Cement

Improving Geopolymer Concrete Performance with Hazardous Solid Waste Phosphogypsum

Reuse of Pretreated Red Mud and Phosphogypsum as Supplementary Cementitious Material

The Effect of Various Si/Al, Na/Al Molar Ratios and Free Water on Micromorphology and Macro-Strength of Metakaolin-Based Geopolymer

Utilization of untreated-phosphogypsum as filling and binding material in preparing grouting materials

Synergistic Preparation of Geopolymer Usining Electrolytic Manganese Residue, Coal Slag and Granulated Blast Furnace Slag

Characterization and Performance Evaluation of Geopolymer Prepared with Thermal-Mechanical Activated Aluminum Sulfate Residue