Abstract:Manganese oxides with varied Mn valance states but identical morphologies were synthesized via a facile thermal treatment of γ-MnOOH. Also, their catalytic performance on ozone decomposition was investigated following the order of Mn3O4 < Mn2O3 < MnO2 < MnO2-H-200. In combination with X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer–Emmett–Teller (BET), transmission electron microscopy (TEM), H2-temperature-programmed reduction (TPR), O2-temperature-programmed desorption (TPD), and X-ray photoelectron spectroscopy (XPS) characterization, it was deduced that the superior O3 decomposition capacity for MnO2-H-200 was strongly associated with abundant oxygen vacancies on its surface. Among Mn3O4, Mn2O3, and MnO2, the difference in O3 decomposition efficiency was dependent on the divergent nature of oxygen vacancy. Density functional theory (DFT) calculation revealed that Mn3O4 and MnO2 possessed lower formation energy of oxygen vacancy, while MnO2 had the minimum desorption energy of peroxide species (O2*). It was deduced that the promotion of the O3 decomposition capability was attributed to the easier O2* desorption. Insights into the deactivation mechanism for MnO2-H-200 further validated the assumptions. As the reaction proceeded, adsorbed oxygen species accumulated on the catalyst surface, and a portion of them were transformed to lattice oxygen. The consumption of oxygen vacancy led to the deactivation of the catalyst.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.langmuir.0c02841?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.langmuir.0c02841</a>.Catalyst preparation; catalyst characterization; XRD patterns of the as-prepared γ-MnOOH; N2 adsorption and desorption isotherms of different MnOx catalysts; top plane view and the oxygen vacancy sites of the preferentially exposed crystal plane for various MnOx during DFT calculation; FT-IR spectra of MnO2-H-200 and partially deactivate MnO2-H-200 catalysts; ozone conversion over MnO2-H-200 and the regenerated MnO2-H-200; the pore size distribution of different MnOx catalysts calculated by the BJH method (<a class="ext-link" href="/doi/suppl/10.1021/acs.langmuir.0c02841/suppl_file/la0c02841_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Regeneration of Ozone Decomposition Catalysts by Elimination of O2 2 2- from Oxygen Vacancies

Regeneration of Ozone Decomposition Catalysts by Elimination of O22- from Oxygen Vacancies

Catalytic Ozonation of Multiple Vocs at Low Temperature over a Potassium-Modified Mnox-Based Catalyst

Novel Electrolytic Regeneration Method for Cyclic Regeneration of Ozone Decomposition MnO x Catalysts

Novel Electrolytic Regeneration Method for Cyclic Regeneration of Ozone Decomposition MnOx Catalysts.

Enhanced H2O2 Utilization Efficiency in Fenton-like System for Degradation of Emerging Contaminants: Oxygen Vacancy-Mediated Activation of O2.

A thorough observation of an ozonation catalyst under long-term practical operation: Deactivation mechanism and regeneration

Oxygen vacancies-driven nonradical oxidation pathway of catalytic ozonation for efficient water decontamination

Regeneration of Single-Atom Catalysts Deactivated under Acid Oxygen Reduction Reaction Conditions

Oxygen vacancies in the catalyst: Efficient degradation of gaseous pollutants

Efficient ozone decomposition in high humidity environments using novel iron-doped OMS-2-loaded activated carbon material

Deactivation and Regeneration of the Commercial Cu/ZnO/Al 2 O 3 Catalyst in Low-Temperature Methanol Steam Reforming

Insights into the Reactive and Deactivation Mechanisms of Manganese Oxides for Ozone Elimination: The Roles of Surface Oxygen Species

Regeneration mechanism of a deactivated zeolite-supported catalyst for the combustion of chlorinated volatile organic compounds

Regeneration of catalysts deactivated by coke deposition: A review

Regeneration of Deactivated CeCoxO2 Catalyst by Simple Thermal Treatment

Α-Fe2o3-supported Co3O4 Nanoparticles to Construct Highly Active Interfacial Oxygen Vacancies for Ozone Decomposition.

Removing Surface Hydroxyl Groups of Ce-Modified MnO2 to Significantly Improve Its Stability for Gaseous Ozone Decomposition

Unlocking efficient and robust ozone decomposition with CNT-confined manganese oxide via synergistic electronic modulation

Deactivation Mechanism and Feasible Regeneration Approaches for the Used Commercial NH3-SCR Catalysts

A Cobalt-Vacant Co3O4 As a Stable Catalyst for Room-Temperature Decomposition of Ozone in Humid Air