Abstract:In this work, mesoporous poorly crystalline hematite (α-Fe2O3) was prepared using mesoporous silica (KIT-6) functionalized with 3-[(2-aminoethyl)amino]propyltrimethoxysilane as a hard template (SMPC-α-Fe2O3). The disordered atomic arrangement structure of SMPC-α-Fe2O3 promoted the formation of oxygen vacancies, which was confirmed using X-ray photoelectron spectroscopy (XPS), O2-temperature-programmed desorption (TPD), H2-temperature-programmed reduction (TPR), and in situ diffuse reflectance infrared Fourier transform (DRIFT) analyses. Density functional theory calculations (DFT) also proved that reducing the crystallinity of α-Fe2O3 decreased the formation energy of oxygen vacancies. TPD and in situ DRIFT analyses of NH3 adsorption suggested that the surface acidity of SMPC-α-Fe2O3 was considerably higher than those of mesoporous poorly crystalline α-Fe2O3 (MPC-α-Fe2O3) and highly crystalline α-Fe2O3 (HC-α-Fe2O3). The oxygen vacancies and acid sites formed on α-Fe2O3 surface are beneficial for ozone (O3) decomposition. Compared with MPC-α-Fe2O3 and HC-α-Fe2O3, SMPC-α-Fe2O3 exhibited a higher removal efficiency for 200-ppm O3 at a space velocity of 720 L g-1 h-1 at 25 ± 2 °C under dry conditions. Additionally, in situ DRIFT and XPS results suggested that the accumulation of peroxide (O22-) and the conversion of O22- to lattice oxygen over the oxygen vacancies caused catalyst deactivation. However, O22- could be desorbed completely by continuous N2 purging at approximately 350 °C. This study provides significant insights for developing highly active α-Fe2O3 catalysts for O3 decomposition.

Α-Fe2o3-supported Co3O4 Nanoparticles to Construct Highly Active Interfacial Oxygen Vacancies for Ozone Decomposition.

Synthesis of Oxygen Vacancy-Enriched N/P Co-Doped CoFe2O4 for High-Efficient Degradation of Organic Pollutant: Mechanistic Insight into Radical and Nonradical Evolution.

Oxygen vacancies-driven nonradical oxidation pathway of catalytic ozonation for efficient water decontamination

Mesoporous poorly crystalline α-Fe2O3 with abundant oxygen vacancies and acid sites for ozone decomposition

A Cobalt-Vacant Co3O4 As a Stable Catalyst for Room-Temperature Decomposition of Ozone in Humid Air

Fabrication of a Carbon-Coated Fe3O4 for Ozone Catalysis to Facilitate HO2− Formation During Ozonation

Efficient Removal of Toxic Pollutants over Fe–Co/ZrO 2 Bimetallic Catalyst with Ozone

High-Performance Co-MnOx Composite Oxide Catalyst Structured onto Al-Fiber Felt for High-Throughput O3 Decomposition

Surface Oxygen Vacancy Induced Α-Mno2 Nanofiber for Highly Efficient Ozone Elimination

High performance ozone decomposition spinel (Mn,Co)3O4 catalyst accelerating the rate-determining step

Oxygen Vacancy Engineering of Co3 O4 Nanocrystals Through Coupling with Metal Support for Water Oxidation.

Catalytic ozone decomposition and adsorptive VOCs removal in bimetallic metal-organic frameworks

Enhanced Ozone Oxidation by a Novel Fe/Mn@γ−Al2O3 Nanocatalyst: the Role of Hydroxyl Radical and Singlet Oxygen

Efficient Ozone Elimination over MnO2 Via Double Moisture-Resistance Protection of Active Carbon and CeO2

Co<SUP>3+</SUP>-O-V<SUP>4+</SUP> cluster in CoVOx nanorods for efficient and stable electrochemical oxygen evolution

Oxygen-vacancy-rich Co3O4@Fe-B-O heterostructure for efficient oxygen evolution reaction in alkaline and neutral media

Efficient ozone decomposition in high humidity environments using novel iron-doped OMS-2-loaded activated carbon material

Nano ferrites (AFe2O4, A = Zn, Co, Mn, Cu) as efficient catalysts for catalytic ozonation of toluene

Enhancing Oxygen Activation Ability by Composite Interface Construction over a 2D Co3O4-Based Monolithic Catalyst for Toluene Oxidation

Efficient catalytic ozonation over Co-ZFO@Mn-CN for oxalic acid degradation: Synergistic effect of oxygen vacancies and HOO-Mn-NX bonds

Enhanced Activation of Peroxymonosulfate Using Oxygen Vacancy-Enriched FeCo2O4−x Spinel for 2,4-Dichlorophenol Removal: Singlet Oxygen-Dominated Nonradical Process