Removing Surface Hydroxyl Groups of Ce-Modified MnO2 to Significantly Improve Its Stability for Gaseous Ozone Decomposition

Yang Liu,Pengyi Zhang

DOI: https://doi.org/10.1021/acs.jpcc.7b07931

2017-01-01

Abstract:Stratospheric ozone (O-3), which slips into the cabin through the air-supply system in a commercial airliner, is detrimental to human health around the world. For gaseous O-3 abatement, catalytic decomposition is an effective method. However, catalyst deactivation is one of the main obstacles to its practical application. In this study, a new deactivation mechanism involving the surface hydroxyl group of catalyst is found by investigating the effects of heat treatment of cerium modified todorokite-type manganese dioxides (Ce MnO2) on O-3 decomposition, which will contribute to the development of more active and stable O-3 decomposition catalysts in the future work. The in situ DRIFT study indicates that gaseous O-3 reacted with surface hydroxyl groups to form surface adsorbed water, which occupied the catalytically active sites (i.e., oxygen vacancies) leading to the catalyst deactivation. Calcination at 300 degrees C greatly removed surface hydroxyl groups while keeping oxygen vacancies almost unchanged at the same time; thus the as-obtained catalyst showed greatly improved stability, keeping similar to 98% of removal efficiency for similar to 115 ppm of O-3 within 5 h under a very high space velocity of 1200 L g(-1) h(-1) at room temperature.