Abstract:In thermoelectric research, the introduction of a dopant can suppress lattice thermal conductivity (κ1) through phonon scattering and optimize the power factor (PF) by changing the behavior of carriers, which are the key prerequisites for high thermoelectric performance. However, the electrical thermal conductivity (κe) can also increase with the increase of electrical conductivity (σ), which may override the optimization in PF and be detrimental to the improvement of final ZT. In this work, we highlight an amphoteric doping method by using Mn atoms to substitute both Ag and Sb atoms in AgSbTe2. The MnSb positive doping in p-type AgSbTe2 can improve the σ through increasing the hole concentration while maintaining a relative high Seebeck coefficient (S), thus substantially improving the PF. On the other hand, the MnAg negative doping can introduce electrons into the matrix, which will recombine with the major hole carriers and lead to a decrease of σ to suppress exorbitant κe induced by the MnSb doping. The combination of the both functions by Mn amphoteric doping can further improve the thermoelectric property through charge compensation modulation. By virtue of amphoteric doping, though σ is decreased, PF is further optimized because of increased S, while the total thermal conductivity (κtotal) is further decreased due to suppressed κe and additional phonon scattering, which are beneficial for the improvement of the final ZT value. As a result, 5 mol % MnAg-MnSb amphoteric doping AgSbTe2 sample achieves a maximum ZT value of ∼0.74 at 550 K, which is higher than that of the pristine sample and other Mn monodoped counterparts. The present work suggests charge compensation modulation via amphoteric doping as an effective avenue to simultaneously achieve low thermal conductivity and high power factor for better thermoelectric performance.

Insights into Enhanced Thermoelectric Performance of the N-Type Mg3Sb2-Based Materials by Amphoteric Al Doping

Enhanced thermoelectric performance of n-type Mg3Bi2-based materials by Se doping and alloying engineering

Improvement of Thermoelectric Properties of n-Mg3.2Sb1.5Bi0.5 by Co-doping of Te and Y

Band Structure and Thermoelectric Properties of Al-doped Mg 3− X Al X Sb 2 Compounds

Extraordinary N-Type Mg3SbBi Thermoelectrics Enabled by Yttrium Doping

Enhancing the Thermoelectric Performance of n‐Type Mg3Sb2‐Based Materials via Ag Doping

Charge Compensation Modulation of the Thermoelectric Properties in AgSbTe2 Via Mn Amphoteric Doping.

Na/Bi-co-doping and Heterogeneous Interfaces Leading to Enhanced Thermoelectric Performance of P-Type Mg3Sb2-based Zintls

Enhancing Thermoelectric Performance in P-type Mg3Sb2-based Zintls Through Optimization of Band Gap Structure and Nanostructuring

Thermoelectric Enhancement Achieved by Y and La Co-doping in N-Type Mg3.2Sb1.5Bi0.5

Simultaneously Improved Thermoelectric and Mechanical Properties Driven by MgB2 Doping in Bi0.4Sb1.6Te3 Based Alloys

Extraordinary Thermoelectric Performance in N-Type Manganese Doped Mg3Sb2 Zintl: High Band Degeneracy, Tuned Carrier Scattering Mechanism and Hierarchical Microstructure

Thermoelectric performance improvement of p-type Mg3Sb2-based materials by Zn and Ag co-doping

Optimization of Thermoelectric Property of n‐Type Mg3Sb2 Near Room Temperature via Mn&Se Co‐Doping

High performance of Mg3Bi1.5Sb0.5 based materials for power generation: Revealing the counter-intuitive effect of tuning Bi content on the thermoelectric properties

Optimizing the thermoelectric performance of p-type Mg<sub>3</sub>Sb<sub>2</sub> by Sn doping

Improvement of the Thermoelectric Properties of P-Type Mg3Sb2 by Mg-Site Double Substitution

Roles of concentration-dependent Cu doping behaviors on the thermoelectric properties of n-type Mg3Sb1.5Bi0.5

Thermoelectric performance enhancement of Pb-doped α -MgAgSb near room temperature

Realizing a High <i>ZT</i> of 1.6 in N-Type Mg<sub>3</sub>Sb<sub>2</sub>-Based Zintl Compounds through Mn and Se Codoping

Metallic N-Type Mg3 Sb2 Single Crystals Demonstrate the Absence of Ionized Impurity Scattering and Enhanced Thermoelectric Performance.