Impact of Thermal Aging Temperatures on the Combustion Behavior and Mechanical Properties of Flame-Retardant Electrical Cables

Long Yan,Wenqiang Wang,Zhisheng Xu

DOI: https://doi.org/10.1007/s10973-024-13437-5

IF: 4.755

2024-01-01

Journal of Thermal Analysis and Calorimetry

Abstract:To assess the fire safety of cables in the service process, the influence of thermal-aging temperature on the combustion properties, pyrolysis properties, and mechanical properties of civilian-type flame-retardant electrical cables was investigated. Flammability test shows that the LOI value of the sheath increases with the rise of thermal-aging temperature, primarily ascribed to the formation of a dense carbon layer. Cone calorimeter test shows that the total heat release (THR) value and residual mass of the cables firstly decrease and then increase as the thermal-aging temperature rises. After 21 days of aging treatment at 120 °C, the THR and peak heat release rate values of the cable are reduced to the lowest values of 88.9 kW m−2 and 109.2 MJ m−2, respectively. TG analysis shows that the onset decomposition temperature of the sheath first increases and then decreases with the rise of the thermal-aging temperature, where the onset decomposition temperature declines sharply after 150 °C thermal aging for 21 days. Mechanical test shows that as thermal-aging temperature increases, the elongation at break of the sheath decreases sharply, while the tensile strength increases significantly. This is mainly because the molecular structure of the aged sheathing material is changed, as supported by SEM and FTIR analyses.