Research on the Thermal Aging Characteristics of Crosslinked Polyethylene Cables Based on Polarization and Depolarization Current Measurement

Yamei Li,Zhaowei Peng,Dangguo Xu,Shiyang Huang,Yanfeng Gao,Yuan Li
DOI: https://doi.org/10.3390/en17102274
IF: 3.2
2024-05-10
Energies
Abstract:Although XLPE cables are widely used in power transmission and distribution systems, their insulating properties are susceptible to degradation due to thermal aging. In order to clarify the influence law of the thermal aging process on the structural and dielectric properties of XLPE cables, this paper investigates the thermal aging characteristics of XLPE cables by using polarization and depolarization current measurement. Results show that when the XLPE cable is aged at 140 °C, the crystallinity of the insulation layer appears to increase and then decrease. With the increase in aging time, micron-sized microvoids appear on the surface of the XLPE. At the same time, the DC conductivity and 0.1 Hz dielectric loss factor of the insulating layer increase with the aging time. The average DC conductivity increased from 2.26 × 10−16 S/m for new cables to 4.47 × 10−16 S/m after aging for 432 h, while the dielectric loss increased from 0.11% to 0.42%. The polarization characteristics of thermal-aged cables were further analyzed using the extended Debye model. Results indicate that the time constant of the third branch of the model increased significantly with increasing aging time. A correspondence between this parameter and the thermal aging time of the cable was established. Thermal aging can damage the crystalline structure of XLPE, so that the number of interfaces between the crystalline and amorphous regions of the material increases, resulting in structural damages and a decline in the dielectric properties of the cable insulation.
energy & fuels
What problem does this paper attempt to address?
The main problems that this paper attempts to solve are: how to determine the thermal aging degree of cross - linked polyethylene (XLPE) cables through polarization and depolarization current (PDC) measurements, and establish the correspondence between the branch parameters of the extended Debye model and the thermal aging time of the cables. Specifically, the research aims to: 1. **Analyze the changes in parameters such as conductivity and dielectric loss factor of XLPE cables under different thermal aging times**: - The research found that with the increase of thermal aging time, the direct current conductivity and 0.1 Hz dielectric loss factor of XLPE cables increase significantly. For example, the average direct current conductivity increases from \(2.26\times 10^{-16}\, \text{S/m}\) for new cables to \(4.47\times 10^{-16}\, \text{S/m}\) after 432 hours of aging, and the dielectric loss increases from 0.11% to 0.42%. 2. **Explore the influence of thermal aging on the structure and dielectric properties of XLPE cables**: - Thermal aging will cause the crystallinity of the XLPE cable insulation layer to increase first and then decrease, and micron - sized micropores will appear on the surface. These changes indicate that thermal aging will damage the crystal structure of XLPE, resulting in an increase in the number of interfaces between crystalline and amorphous regions in the material, thereby impairing its dielectric properties. 3. **Use the extended Debye model to analyze the polarization characteristics of thermally aged cables**: - Through the PDC measurement results, the researchers further analyzed the polarization characteristics of thermally aged cables using the extended Debye model. The results show that the time constant of the third branch in the model increases significantly with the aging time, and the correspondence between this parameter and the cable thermal aging time is established. 4. **Reveal the physical mechanism of the change in XLPE dielectric properties caused by thermal aging**: - Through differential scanning calorimetry (DSC) and scanning electron microscopy (SEM) tests, the influence of thermal aging on the structural parameters of XLPE insulation materials was analyzed, and the physical mechanism of the change in dielectric parameters was explained from the perspective of the polymer aggregation state structure. In summary, this research aims to comprehensively understand the performance degradation law of XLPE cables during the thermal aging process through experimental and modeling means, and provide a scientific basis for the safe and stable operation of power systems.