Effect of T6 Heat Treatment on Microstructure and Mechanical Properties of 6082 Aluminum Alloy Automotive Flange Components Formed by Squeeze Casting

Jufu Jiang,Jingbo Cui,Ying Wang,Minjie Huang,Jian Dong,Jing Yan

DOI: https://doi.org/10.1016/j.msea.2024.146974

2024-01-01

Abstract:In this research, 6082 aluminum alloy automotive flange components with complex shape and large wall thickness difference were formed via squeeze casting. The effect of T6 heat treatment process parameters (solution time, solution temperature, aging time and aging temperature) on microstructure and mechanical properties were studied through controlling variable method. The yield strength (YS), ultimate tensile strength (UTS) and elongation (EL) of 6082 aluminum alloy automotive flange components after T6 heat treatment were firstly increased and then decreased with the increasing solution temperature, solution time and aging time, respectively. However, with an increase of aging temperature, YS and UTS were significantly increased, while EL was decreased. The optimal T6 heat treatment process parameters (solution temperature of 525 degrees C, solution time of 180 min, aging temperature of 185 degrees C and aging time of 420 min) were obtained. Under the optimal T6 heat treatment process parameters, the YS, UTS, EL were 304.2 MPa, 348.7 MPa and 7.42 %, respectively. The fracture mode is a mixture of ductile and cleavage fracture. After T6 heat treatment, a plethora of tiny precipitates appeared, which included the Al(FeMn)Si phase with a size of about 100 nm and the finer beta ''-Mg2Si phase. These tiny precipitates lead to lattice distortion to hinder the movement of dislocations and they had a significant strengthening effect on the improvement of mechanical properties. In short, 6082 aluminum alloy automotive flange components produced by squeeze casting after T6 heat treatment has significantly competitive advantages for its outstanding mechanical properties.