Corrosion Behavior of Cu-Ni-Fe-Mn-Cr Alloy in 3.5 Wt.% NaCl Solution

Shifang Li,Zhu Xiao,Mei Fang,Haofeng Xie,Lijun Peng
DOI: https://doi.org/10.5006/4553
2024-01-01
CORROSION
Abstract:A novel Cu-10Ni-1.7Fe-0.5Mn-0.2Cr alloy was fabricated and exposed to neutral 3.5 wt.% NaCl solution for various days. The corrosion performance, corrosion film, and corrosion mode of the alloy were investigated in detail. The results suggested that the average corrosion rate reduced from 0.082 mm/a for one-day immersion sample to 0.037 mm/a for thirty-day immersion sample. The reduction in corrosion rate was mainly attributed to the progressive thickness and densification of the corrosion film, leading to increasing the resistance of corrosion film with the prolonging exposure time. Low-valent oxides and chlorinated compounds were generated over the one-day immersion sample surface, while high-valent oxides and hydroxide compounds were developed over the thirty-day immersion sample surface. The mature corrosion film typically composed of Cu2O, CuO, Cu2(OH)3Cl, γ-FeOOH, MnO2, and Cr2O3. Eventually, the alloys suffered from the selective corrosion and intergranular corrosion after a long exposure time in NaCl solution.
What problem does this paper attempt to address?