Abstract:Previous studies suggested that Zintl phases related to the Ca9Zn4.5− δ Sb9 (0 δ x Cu x Sb9 indicated that they could achieve an optimized zT around 0.7. Especially for Ca9Zn4.5− δ Sb9, a very recent report suggested that a high zT of 1.1 at 875 K could be obtained in combination of various secondary phases introduced by the variation of Zn contents, which provided a chemical potential to change the composition. However, to change the composition of Ca9Zn4.5− δ Sb9 is actually very difficult to implement owing to the narrow homogeneity range. In this work, with Ca substituted by big cations such as Eu2+ and Sr2+, the unit cell of Ca9Zn4.5− δ Sb9 was expanded, and similar significant enhancement on the thermoelectric performance was resulted. All syntheses were handled inside a glovebox, then the reactants were loaded in the Nb tube and arc-welded, which were enclosed in a fused silica tube. The reactions were firstly heated to 1173 K in 6 h and then maintained at this temperature for 24 h. After the homogeneity process, the furnace was slowly cooled down to 873 K at a rate of 6 K/h, followed by another dwelling for 6 hours and finally cooled down to 573 K at a rate of 10 K/h. At last, the furnace was shut down and the reactions were opened in the glovebox. The compound were fully characterized by single-crystal X-ray diffraction (SXRD) and powder X-ray diffraction(PXRD), Energy dispersive spectrometer (EDS) and Hall effect measurement, etc. Single-crystal X-ray diffraction (SXRD) proves that with the increase of Sr component, the crystal parameters are slightly increasing. Hall effect measurement show that the substitution of Ca by Eu or Sr can both lead to an obvious decreasing on the carrier (holes) concentration, and the resultant mobility for Sr/Eu-doped materials is very similar if compared by the same doping level. It is also noted that neither the carrier concentration nor the mobility seems to vary linearly with the Eu/Sr-doping contents, which means a saturated state will be eventually approached. This phenomenon is consistent with the speculation above that the changes on the properties should predominantly originate from the change of interstitial Zn content, which the size effect dominated. While the decreasing carrier concentrations as well as the increasing mobility and lattice thermal conductivity all point to a structure modification, the crystal structures of these doped materials were systematically verified through the single crystal X-ray diffraction. In conclusion, although a direct measurement on such a small composition variation is very difficult (the X-ray diffraction results prove it), the significantly reduced carrier concentration and increased mobility as well as lattice thermal conductivity can still provide some useful hints on understanding the property optimization of these materials. For material Ca8.2Eu0.8Zn4.5− δ Sb9, high figure of merit with ZT ~0.81 has been achieved at 873 K.

Band engineering and phonon softening enable the achievement of significant enhancement in the thermoelectric performance of EuMg2Sb2 by Zn doping

Regulating thermoelectric properties of Eu0.5Ca0.5Zn2Sb2 through Mg dopant

Mechanism of Thermoelectric Performance Enhancement in CaMg2Bi2‐Based Materials with Different Cation Site Doping

Na/Bi-co-doping and Heterogeneous Interfaces Leading to Enhanced Thermoelectric Performance of P-Type Mg3Sb2-based Zintls

Enhancing Thermoelectric Performance of Mg3Sb2 Through Substitutional Doping: Sustainable Energy Solutions via First-Principles Calculations

Optimization of the thermoelectric performance of α-MgAgSb-based materials by Zn-doping

Thermoelectric performance improvement of p-type Mg3Sb2-based materials by Zn and Ag co-doping

Significantly enhanced thermoelectric figure of merit of n-type Mg3Sb2-based Zintl phase compounds via co-doped of Mg and Sb site

Enhancing the effective mass and covalent bond strength of Cu 3 SbSe 4 -based thermoelectric materials by Mn/Sn co-doping

Enhancing thermoelectric performance of AB 2 Sb 2 -type Zintl phase through band shaping and lattice distortion

Enhancement of the thermoelectric properties of MnSb2Se4 through Cu resonant doping

Enhanced Thermoelectric Performance of Cu 2 CdSnSe 4 by Mn Doping: Experimental and First Principles Studies

Band Engineering Through Pb‐Doping of Nanocrystal Building Blocks to Enhance Thermoelectric Performance in Cu3SbSe4

Synergistic Effect of Band and Nanostructure Engineering on the Boosted Thermoelectric Performance of n‐Type Mg3+δ(Sb, Bi)2 Zintls

Realizing Cd and Ag codoping in p-type Mg3Sb2 toward high thermoelectric performance

Excellent thermoelectric performance of boron-doped n-type Mg3Sb2-based materials via the manipulation of grain boundary scattering and control of Mg content

Electronic Orbital Alignment and Hierarchical Phonon Scattering Enabling High Thermoelectric Performance p-Type Mg 3 Sb 2 Zintl Compounds

Significant enhancement of the thermoelectric properties for MnSb2Se4 through Ag doping

Sr/Eu Cation Doping and Thermoelectric Properties of the Compound Ca9Zn4.5−δSb9 (0<Δ<0.5)

Point defect approach to enhance the thermoelectric performance of Zintl-phase BaAgSb

Enhanced Thermoelectric Performance of Zintl Phase Ca9Zn4+ xSb9 by Beneficial Disorder on the Selective Cationic Site