Abstract:Neat well cement experience significant strength retrogression at high temperatures above 110 °C, especially at approximately 150 °C. To reveal the mechanism of performance degradation and guide the preparation of high-performance cement, we investigate the hydration process, mechanical behavior, and fracture process for well cement at the temperature of 150 °C based on molecular dynamics simulations and experiments. From triaxial pressure tests and Brazilian splitting tests, the strength, elastic modulus, and Poisson's ratio of well cement decrease drastically with temperature increases from 80 °C to 150 °C. According to XRD, TG/DTG/DSC, and SEM, the hydration degree is insufficient, and larger pores exist in the microstructures. As the main binding phase of well cement, the mechanism of calcium silicate hydrates (C-S-H) influenced by curing temperatures is investigated through molecular dynamics simulations. C-S-H with calcium/silicon ratios (C/S) of 1.1 and 1.8 are simulated in the aqueous and solid states to investigate precipitation and mechanical behaviors. By reducing the C/S ratio to 1.1, the strength rebounds to a certain extent, and the adequacy of the hydration degree improved. It is found from the polymerization process that the increasing temperature promotes the polymerization rate, which is higher with C/S = 1.8 than that of 1.1. However, an increase in the C/S ratio will lead to a decrease in bridging oxygen content, thus a lower polymerization degree. The fracture simulations of C-S-H gels at different temperatures indicate that the failure of the C-S-H structure is mainly attributed to the disassembling of the calcium oxygen layers. With a higher temperature, there are fewer Ca-O bonds breaking, thus less strain energy consumed, resulting in worse performance. The elasticity of C-S-H, including Young's and shear moduli, also exhibits certain degradations at a higher temperature. The elastic behavior of C-S-H with a low C/S ratio is generally higher than the high C/S.

Structural Deterioration and Mechanical Degradation of Limestone Calcined Clay Cement (LC3) under Elevated Temperature

Multiscale Prediction of Thermal Damage for Hybrid Fibers Reinforced Cementitious Composites Blended with Fly Ash at High Temperatures

Uniaxial Tensile Behavior, Flexural Properties, Empirical Calculation and Microstructure of Multi-Scale Fiber Reinforced Cement-Based Material at Elevated Temperature

Correlation Between Macroscopic Properties and Microscopic Pore Structure in Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites Subjected to Elevated Temperatures

Mechanical Properties and Microstructures of Steel-basalt Hybrid Fibers Reinforced Cement-based Composites Exposed to High Temperatures

Multiscale assessment of performance of limestone calcined clay cement (LC3) reinforced with virgin and recycled carbon fibers

Microstructural investigation and performance of LC3 cementitious materials

Effects of High Temperature and Substitution Rates of Fly Ash on the Mechanical Properties and Microstructures of Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites

A review of high temperature properties of cement based composites: Effects of nano materials

Microstructure and mechanical behaviour of 3D printed ultra-high performance concrete after elevated temperatures

Insights into the effect of high temperature on the shear behavior of the calcium silicate hydrate by reactive molecular dynamics simulations

Insight into Class G Wellbore Cement Hydration and Mechanism at 150 °C Using Molecular Dynamics

Layer interface characteristics and adhesion of 3D printed cement-based materials exposed to post-printing temperature disturbance

Thermo-Mechanistic Multi-Scale Modeling of Structural Concrete at High Temperature

Deterioration of Cement-Fly Ash Composite Binder Materials Exposed to Elevated Temperature

Experimental investigation on the deterioration of the physical and mechanical properties of autoclaved aerated concrete at elevated temperatures

Development And Design Of Composite Cementitious Material At Long-Time Circular Elevated Temperature In Metallurgy Environment

Global insights into micro-macro mechanisms and environmental implications of limestone calcined clay cement (LC3) for sustainable construction applications

Microstructural Characterization of Limestone Exposed to Heat with XRD, SEM and TG-DSC

Mitigation of lack of fusion in 3D printed limestone calcined clay cement concrete induced by effective microorganisms

Multiscale Investigation on the Performance of Engineered Cementitious Composites Incorporating PE Fiber and Limstone Calcined Clay Cement (LC3)