Effect of Hydrogen on Residual Ductility of Zr-Sn-Nb Alloy after LOCA Test

Xin Liu,Menghe Tu,Shen Li,Hui Wang,Yong Hu

DOI: https://doi.org/10.12442/j.issn.1002-185x.20230177

2024-01-01

Rare Metal Materials and Engineering

Abstract:Zirconium cladding absorbs hydrogen in the reactor, and the zirconium cladding will embrittle in the loss of coolant accident (LOCA). The hydrogen-containing cladding is more likely to rupture in the process of accident or the subsequent treatment of accident, resulting in the leakage of radioactive products. In this research, residual ductility of zirconium alloys with different hydrogen contents (0, 195, 315, 395 mu g/g) after simulated LOCA was studied, and the effect mechanism of hydrogen on residual ductility of zirconium alloys during simulated LOCA was explored. The results show that the residual ductility of zirconium alloy decreases with the increase in hydrogen content. The addition of hydrogen has little effect on the microstructure of zirconium alloy, and the effect of hydrogen on the microstructure of zirconium alloy is not the reason for the reduction of residual ductility of zirconium alloy. One of the reasons why the presence of hydrogen leads to the decrease in the residual ductility of zirconium alloy after simulated LOCA is that the increase in hydrogen content increases the oxygen content absorbed by the prior-beta phase after quenching, thus reducing the residual ductility of zirconium alloy. Secondly, hydrogen may exist in the prior-beta phase in the form of saturated solid solution or fine hydride brittle phase, which also decreases the residual ductility of zirconium alloy.