Preparation of Pt-Pd/BaO/TiAlO catalyst for NOx storage-reduction and its sulfur resistance
Chen Ying,He Jun,Ma Yugang,Chen Xiaoping,Wang Lefu,Ll Xuehui
IF: 16.5
2007-01-01
Chinese Journal of Catalysis
Abstract:NOx in exhaust gases from lean burn engines can be clarified over Toyota-type storage-reduction catalysts, but it is difficult for the catalyst to be applied in domestic automobiles due to deterioration caused by SO2 in the emission. A novel Pt-Pd/BaO/TiAlO catalyst for NOx storage-reduction (NSR) was prepared by coprecipitation-impregnation. The catalyst was evaluated by NOx storage in lean burn and by NOx storage-reduction in lean-rich cycles both in the absence and in the presence of SO2, respectively, using a series cyclic sequences of feed which changes from lean conditions (GHSV of 12 000 h(-1), 800 Mg/m(3) of NO, 4 % of O-2, 200 Mg/m(3) of SO2 for sulfur resistance test, remainder At, 350 degrees C, and for 30 min) to rich conditions (GHSV of 12 000 h(-1), 4 % of H-2, remainder At, 350 degrees C, and for 20 min). The TiAlO bi-oxide and the catalyst were characterized by temperature-programmed desorption, temperature-programmed reduction, N-2 adsorption-desorption, and X-ray diffraction. The results showed that TiAlO bi-oxide in Pt-Pd/BaO/TiAlO catalyst acted as both a support and an adsorbent in the NOx storage-reduction process. The maximum capacity for NOx storage was obtained when the molar ratio of Ti/Al in TiAlO was 1:2. BaO (4 %) not only enhanced the thermal stability of catalyst but also increased NOx storage capacity. Pt-Pd/BaO/TiAlO had better sulfur resistance compared with the Toyota-type NSR catalyst Pt/BaO/gamma-Al2O3. One of the reasons might be that sulfur compounds produced in NOx storage on the surface of the catalyst were unstable and easily to be removed by reduction.