Identification of the dual roles of Al2O3 coatings on NMC811-cathodes via theory and experiment

Farheen N. Sayed,Richard L.B. Chen,Hrishit Banerjee,Israel Temprano,Andrew J. Morris,Clare P. Grey

DOI: https://doi.org/10.26434/chemrxiv-2024-xnw4h

2024-06-20

Abstract:Metal-oxide coatings are a favoured strategy for mitigating surface degradation problems in state-of-the-art lithium-ion battery Ni-rich layered positive electrode materials. Despite their extensive use, a full, fundamental understanding of the role of coatings in reducing degradation and extending cycling lifetimes is currently lacking. In this work, the interactions between an atomic layer deposited (ALD) alumina coating on polycrystalline LiNi0.8Mn0.1Co0.1O2 (NMC811) and a carbonate-based battery electrolyte are studied. Solid-state nuclear magnetic resonance (ssNMR) heteronuclear experiments show that the Al2O3 coating transforms by reacting with electrolyte species present before and during electrochemical cycling, scavenging protic and acidic species. Density-functional theory calculations highlight the additional chemical effect of the coating in locally stabilising the structure of the NMC811, limiting oxidation of the oxygen atoms coordinated to both Al and Ni, thereby limiting the surface reconstruction process and improving the electrochemical performance. Improved NMC811 surface stability is confirmed by monitoring gaseous degradation species by operando electrochemical mass-spectrometry and via X-ray spectroscopic analysis of the electrochemically aged samples to examine changes in Ni and O oxidation state and local structure. The combination of this experimental and theoretical analysis suggests that Al2O3 coatings have a dual role: as a protective barrier against attack from chemical species in the electrolyte, and as an artificial passivating layer hindering oxygen loss and surface phase transformations. This holistic approach, which provides a fundamental understanding of how the surface stability is improved by the coating, will aid the design of the state-of-the-art and future positive electrode materials.

Chemistry

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the surface degradation of lithium nickel cobalt manganese oxide (NMC811) cathode materials in high - energy - density lithium - ion batteries. Specifically, the research aims to deeply understand the mechanism of action of aluminum oxide (Al₂O₃) coatings in improving the electrochemical performance of NMC811 and prolonging the cycle life through a combination of experimental and theoretical methods.

### Main problems:
1. **Surface degradation problem**: Layered oxide cathode materials with high nickel content (such as NMC811) are prone to surface degradation during the charge - discharge process, resulting in capacity attenuation, increased impedance, and reduced safety.
2. **Unclear coating mechanism**: Although metal oxide coatings (such as Al₂O₃) have been widely used to alleviate these problems, their specific protection mechanisms have not been fully understood. In particular, the structural evolution of the coating during the electrochemical cycle and its impact on the surface and subsurface of NMC811 particles are still unclear.

### Research objectives:
- **Reveal the dual role of Al₂O₃ coatings**: Prove through experiments that the Al₂O₃ coating not only acts as a barrier to prevent chemical substances in the electrolyte from attacking the NMC811 surface, but also as an artificial passivation layer to suppress oxygen loss and surface phase transformation.
- **Provide a detailed mechanism of coating functions**: Combine techniques such as solid - state nuclear magnetic resonance (ssNMR), online electrochemical mass spectrometry (OEMS), X - ray absorption spectroscopy (XAS), and density functional theory (DFT + U) to analyze in detail the changes of Al₂O₃ coatings during the electrochemical cycle and their impact on the surface stability of NMC811.

### Method overview:
- **Material characterization**: Use scanning electron microscopy (SEM), transmission electron microscopy (TEM), X - ray diffraction (XRD), etc. to confirm the successful preparation of Al₂O₃ coatings and their microstructures.
- **NMR experiments**: Monitor the changes in the local coordination environment of Al₂O₃ coatings before and after the electrochemical cycle through single - resonance and double - resonance ssNMR experiments.
- **Electrochemical tests**: Assemble Swagelok cells for electrochemical cycle tests to evaluate the impact of coatings on electrochemical performance.
- **Theoretical calculations**: Use the DFT + U method to calculate the changes in the Ni/O electronic states on the NMC811 surface and explain how the coating stabilizes the surface structure and improves electrochemical performance.

Through these comprehensive experimental and theoretical analyses, the research team hopes to provide a scientific basis for the design of more advanced cathode materials and fundamentally understand how to improve the surface stability of NMC811 through coatings.