Exploring Ho Substituted Y-Fe-B Nanocrystalline Alloys and Hot Worked Magnets

Wenbing Fan,Bang Zhou,Hongya Yu,Jiangxiong Wei,Zhongwu Liu
DOI: https://doi.org/10.1088/2053-1591/ad594f
IF: 2.025
2024-01-01
Materials Research Express
Abstract:Aiming to balance the utilization of rare earth (RE) resources and develop Y-Fe-B based permanent magnets, Ho is employed as strategic substitution for enhancing the magnetic properties and thermal stability of nanocrystalline Y-Fe-B alloys. Ho substituting Y can enhance the coercivity of Y-Fe-B alloys while maintaining their excellent thermal stability. 30 at.% Ho substitution leads to an abnormal increase of remanence Jr and (Y0.7Ho0.3)2Fe14B alloy exhibits good magnetic properties with remanence Jr=0.73 T, intrinsic coercivity Hcj=303 kA/m, and maximum energy product (BH)max=66 kJ/m3. High thermal stability with temperature coefficient of remanence α=-0.124 %/K and temperature coefficient of coercivity β=-0.245 %/K were obtained between 300-400 K. RE-rich (Y0.8Ho0.2)2.5Fe14B alloy also show similar composition dependent magnetic properties with higher coercivity. In addition, nanocrystalline (Y0.5Ho0.5)2.5Fe14B magnets were prepared by hot-pressing and hot deformation process. Due to the lack of low melting point RE-rich phase, this alloy is difficult to be densified and deformed. The formation of high temperature RE2O3 and RE6Fe23 phases and the lack of continuously distributed RE-rich grain boundary phase are responsible for the poor texture of hot deformed magnet. The hot deformed magnet has the magnetic properties of Jr=0.50 T, Hcj=739 kA/m, and (BH)max=40 kJ/m3 together with high thermal stability. The micro-analysis demonstrated the chemical segregation of Y and Ho elements. Higher proportion of Ho than Y existed in main phase and grain boundary phase indicate excess Y were precipitated as Y-rich oxides.
What problem does this paper attempt to address?