Abstract:Motivated by the global rare earth (RE) criticality, the utilization of abundant Ce and Y has attracted tremendous interests in the Nd-Fe-B community. Although the Y substitution can enhance the thermal stability of Nd-Ce-Fe-B magnet, the room-temperature coercivity is lowered drastically, which remains a challenging hurdle. Considering the equivalent intrinsic HA between Ce2Fe14B and Y2Fe14B compound, there is an intriguing possibility of achieving the balanced contributions from Y substitution on the improved coercivity and thermal stability of Nd-Ce-Y-Fe-B magnets simultaneously. Inspired by this possibility, a series of [Nd0.5(Ce1-xYx)0.5]30.5Fe68.5B1.0 melt-spun ribbons (x = 0–0.5, wt%) are prepared through adjusting the Ce/Y ratio in present work. Results show that maximized room-temperature coercivity Hcj of 12.0 ~12.2 kOe, together with preferable temperature coefficient α of −0.17 ~ −0.16%/K and β of −0.37 ~ −0.35%/K within 293–393 K interval are acquired at the optimal Y content (x = 0.1 and 0.2). Above outstanding combination of coercivity and thermal stability are the highest values reported so far upon 50 wt% Ce-Y substitution for Nd, which is ascribed to the intrinsic contribution from Y replacement for Ce in 2:14:1 lattice, as well as the microstructural advantages from refined RE2Fe14B grain and continuous RE-rich grain boundary layer However, excessive Y substitution leads to dramatic grain growth and weakened exchanging coupling effect, drastically deteriorating the coercivity and remanence, despite the fact that both α and β are continually improved. Above findings shed new light on developing resource-saving Nd-Ce-Y-Fe-B permanent magnets with high synergy of coercivity and thermal stability.

High synergy of coercivity and thermal stability in resource-saving Nd-Ce-Y-Fe-B melt-spun ribbons

Performance improvement and element segregation behavior in Y substituted nanocrystalline (La,Ce)–Fe–B permanent magnetic alloys without critical RE elements

Effects of (Nd, Pr)-Hx addition on the coercivity of Nd-Ce-Y-Fe-B sintered magnet

Comparison of (pr, Nd)H Grain Boundary Restructuring and Diffusion on the Magnetic Properties of Nd–La–Ce–Fe–B Sintered Magnet

Improved Thermal Stability of Nd-Ce-Fe-B Sintered Magnets by Y Substitution

Optimization of the core-shell structures and grain boundary to improve the coercivity of high Ce-content Nd-Ce-Fe-B magnets

Concurrent Improvements of Corrosion Resistance and Coercivity in Nd-Ce-Fe-B Sintered Magnets Through Engineering the Intergranular Phase

Enhanced Coercivity of Nd-Ce-Fe-B Sintered Magnets by Adding (nd, Pr)-H Powders

Microstructure and magnetic performance of Nd–Y–Ce–Fe–B sintered magnets after annealing

A Reliable Route for Relieving the Constraints of Multi-Main-phase Nd–La–Ce–Fe–B Sintered Magnets at High La–Ce Substitution: (pr, Nd)H Grain Boundary Diffusion

Magnetic performance change of multi-main-phase Nd–Ce–Fe–B magnets by diffusing (Nd, Pr)H x

Grain boundary restructuring and La/Ce/Y application in Nd–Fe–B magnets

Synergistic grain boundary modification and magnetic hardening for coercivity enhancement in Nd-Ce-Fe-B sintered magnets with Dy Cu addition

Promoting the La Solution in 2:14:1-Type Compound: Resultant Chemical Deviation and Microstructural Nanoheterogeneity

Suppressing laves phase and overcoming magnetic properties tradeoff in nanostructured (Ce,La,Y)–Fe–B alloys via Ge substitution

High Cerium content Fe‐Ce‐Nd‐B sintered magnets with high coercivity

Interaction and Magnetic Properties of NdCeFeB Melt-Spun Ribbons

Research on the La/Ce-rich multi-main-phase RE-Fe-B permanent magnetic materials

Grain boundary engineering towards high-figure-of-merit Nd-Ce-Fe-B sintered magnets: Synergetic effects of (Nd, Pr)Hx and Cu co-dopants

High Coercivity Nd-Ce-Fe-B Nanostructured Ribbons Prepared from Melt Spinning Technique

Effect of Nd-Co on microstructure and magnetic properties of Nd-Ce-Y-Fe-B sintered magnets