Exceptional elevated temperature behavior of nanocrystalline stoichiometric Y 2 Fe 14 B alloys with La or Ce substitutions

Abdul Jabbar Khan

DOI: https://doi.org/10.1007/s10853-019-03916-8

IF: 4.5

2019-01-01

Journal of Materials Science

Abstract:Considering that both La 2 Fe 14 B and Ce 2 Fe 14 B compounds exhibit similar weak temperature-dependent anisotropic fields ( H A ) as Y 2 Fe 14 B, this work aims to clarify the elevated temperature behavior of melt-spun nanocrystalline La- or Ce-partially substituted stoichiometric Y 2 Fe 14 B alloys containing no critical rare earth elements. The results show that La-substituted (Y 1− x La x ) 2 Fe 14 B alloys ( x = 0–0.5) show exceptional elevated temperature behavior, manifested by the increased coercivity with increasing temperature. For the Ce-substituted (Y 1− x Ce x ) 2 Fe 14 B alloys, only x = 0.1 and 0.2 alloys show the similar trend. Both the temperature coefficient of remanence α and coercivity β can be improved by La-substituted, indicating partial substitution La can effectively enhance the thermal stability of Y 2 Fe 14 B alloy. However, excess La or Ce substitution would reduce α and β value, resulting in the deterioration of thermal stability. Highest β values of 0.05 and − 0.08 have been obtained in (Y 0.9 La 0.1 ) 2 Fe 14 B alloy at 300–400 K and (Y 0.8 La 0.2 ) 2 Fe 14 B alloy at 300–500 K, respectively. In addition, Ce substitution can effectively enhance the coercivity of Y 2 Fe 14 B alloy at room temperature and La substitution does not show a beneficial effect on the room-temperature magnetic properties. This work is beneficial for developing high-performance/cost ratio permanent magnets based on abundant rare earth elements with superior thermal stability.