A novel testing technique for dynamic mechanical properties of inorganic glass by electromagnetic Hopkinson bar
Bin Jiang,Jiayi Hu,Yazhou Guo,Yulong Li
DOI: https://doi.org/10.1360/TB-2020-0223
2020-01-01
Abstract:Optical glass materials have a lot of superior properties such as outstanding optical transparency, light weight low manufacturing cost and high impact resistance. Thus, they are widely utilized in the transparent armors, windshields of high-speed train and airplane as well as mobile phone touch screens. Glass structures are often subjected to loading, including quasi-static and dynamic loading during their service. It is well known that the mechanical properties of engineering materials under impact loading are usually much different from those under static loading. To guide the optimal design of glass structures, it is necessary' to conduct a thorough and in-depth study of the mechanical properties of glass materials. However, as a kind of typical brittle material, the failure strain of inorganic glass is extremely small. Therefore. measuring the dynamic mechanical properties of glass material has always been a quite difficult problem in the fields of experimental mechanics and impact dynamics. This paper would propose a new experimental technique-electromagnetic split Hopkinson pressure bar (ESHPB) to solve the afore-mentioned problem. In this paper, quasi-static compressive tests were first conducted using the electronic universal testing machine at a strain rate 10(-3)s(-1), followed by dynamic unidirectional and bidirectional compressive tests by the ESHPB apparatus under an average strain rate of 300 s(-1) for soda-lime silicate glass. respectively. During dynamic compressive tests, the ultra-high-speed camera and flashlights were utilized to observe the damage/crack initiation, propagation and fracture process inside the glass samples. The feedback signal of the ultra-high-speed camera is input into the digital acquisition system, aiming to associate accurately the stress history of the sample with the high-speed image and to study the dynamic failure process in depth. The following conclusions are made based on the test results: (1) When using the ESHPB set-up to measure the dynamic mechanical properties of glass materials, stress equilibrium and approximate constant strain rate loading condition can be achieved without using the pulse shaping technique. It provides a simpler and easier test method for studying the dynamic mechanical properties of brittle materials. (2) Compared with the unidirectional loading tests, bidirectional symmetric loading experimental technique can significantly shorten the time duration for achieving the condition of stress equilibrium and constant strain rate deformation. Therefore. more effective information can be obtained from the test results and the accuracy and reliability of the test results can be greatly improved. (3) Compared with the quasi-static test results, it is found that the compressive strength of the tested glass material increases significantly under dynamic impact loading, showing a strong strain rate effect. The dependence of compressive strength on strain rate was quantitatively characterized by the strain rate sensitivity exponent. (4) The deformation images of samples captured by ultra-high-speed camera indicated that when the cracks first appeared. the specimens did not completely lose the load bearing capacity. The cracks continue to nucleate, propagate and converge. When the cracks fill almost the entire sample. the material loses the load bearing capacity completely and breaks into powders. By comparison, the samples are split into a few columns under quasi-static loading.