Structural and Thermodynamic Assessment of Ba and Ba/Mg Substituted SrFeO3−δ for “Low-Temperature” Chemical Looping Air Separation

Hilal Bektas,Runxia Cai,Leo Brody,Fanxing Li

DOI: https://doi.org/10.1021/acs.energyfuels.4c00859

IF: 4.6541

2024-01-01

Energy & Fuels

Abstract:The increasing demand for high-purity oxygen has prompted interest in chemical looping air separation (CLAS), a promising approach to reduce cost and energy consumption. The current study presents a structural and thermodynamic analysis of Sr0.75Ba0.25FeO3-delta (SBF628), Sr0.75Ba0.25Fe0.875Mg0.125O3-delta (SBFM6271), and Sr0.25Ba0.75FeO3-delta (SBF268) for CLAS applications. Our results confirm that through partial substitution of A- and B-site cations, we can tailor the thermochemical properties of SrFeO3-delta under practical operating conditions, e.g. 400-700 degrees C and 0.2-0.01 atm O-2. Based on X-ray diffraction (XRD) and Rietveld refinement, 25% Ba can be fully substituted into a SrxBa1-xFeO3-delta structure (SBF628), whereas SBF268 and SBFM6271 form minor secondary phases. An increased Ba:Sr ratio in the A-site favors facile oxygen exchange by reducing partial molar enthalpy and improving redox capacity at low temperatures (400-500 degrees C) while leading to an increase in Fe-O bond length in the B-site. Our findings support that the Fe-O bond distance can be a useful descriptor in the optimization of redox performance in SrFeO3-delta (SF) based oxygen carrier candidates for CLAS. All the substituted candidates exhibit superior redox performance to unsubstituted SF at temperatures below 600 degrees C. SBF628 achieves the redox (oxygen storage) capacity of 1.24 wt % under a combined temperature (400-600 degrees C) and pressure swing (0.2-0.01 atm O-2) mode. The introduction of 12.5% Mg in the B-site improves the oxidation kinetics, but it does not have a substantial impact on the oxygen storage capacity. SBFM6271 and SBF628 exhibited excellent recyclability and robustness while a minimal decrease (3%, on a relative basis) in the capacity of SBF268 was observed during 100 redox cycles under pressure swing between 0.2 and 0.01 atm O-2 at 600 degrees C.