Effects of B-site substitution of SrFe2O4 oxygen carrier on the biomass chemical looping gasification performance
Xingqiang Lu,Ge Pu,Mengliang Gao,Jiale Wu,Yunlong Xia,Qianhui Yang
DOI: https://doi.org/10.1007/s13399-024-05607-0
IF: 4.05
2024-04-22
Biomass Conversion and Biorefinery
Abstract:Oxygen carriers are critical in biomass chemical looping gasification. In this work, SrFe1.7X0.3O4 (X = Mn, Co, Ni) were selected as oxygen carriers for biomass chemical looping gasification (BCLG). The results showed that a small amount of Mn, Co, and Ni could be effectively doped into the spinel structure of SrFe2O4 and improved the BCLG performance significantly. The SrFe1.7Mn0.3O4 oxygen carrier achieved the greatest syngas yield of 1.982 m3/kg under optimal reaction conditions (T = 850 °C, O/B = 0.2, and S/B = 3), and the carbon conversion efficiency and gasification efficiency reached 94.17% and 96.64%, respectively. The XPS results revealed that the SrFe1.7Mn0.3O4 oxygen carrier has a greater lattice oxygen content than the SrFe2O4 oxygen carrier, which was the primary reason for improved gasification performance. In the cyclic experiment, owing to the sintering of the oxygen carrier particles, the reactivity of the oxygen carriers gradually decreased after 10 redox cycles, and the syngas yield gradually decreased. The cyclic stability of the oxygen carriers was considerably increased when 75wt.% MgAl2O4 inert carrier was loaded on the SrFe1.7Mn0.3O4. After 10 cycles, the syngas yield, carbon conversion efficiency, and gasification efficiency of the SFM3/75MA oxygen carrier were 1.852 m3/kg, 93.30%, and 95.01%, respectively. In summary, the SFM3/75MA oxygen carrier performed well in biomass gasification and had great cycling stability.Graphical Abstract
energy & fuels,engineering, chemical