Uniformly dispersed NiFeAlO 4 as oxygen carrier for chemical looping steam methane reforming to produce syngas
Jinxia Quan,Yekai Chen,Haoting Mai,Qimeng Zeng,Juan Lv,Enchen Jiang,Zhifeng Hu
DOI: https://doi.org/10.1016/j.ijhydene.2024.02.355
IF: 7.2
2024-03-07
International Journal of Hydrogen Energy
Abstract:Chemical looping steam methane reforming (CL-SMR) is one of the most potential methods for large-scale syngas production. As the key to CL-SMR, the development of oxygen carrier (OC) is typically limited by the factors of CH 4 conversion, H 2 selectivity and resistance to carbon deposition. However, the nonuniform distribution of metals in OC leads to unstable conversion rate and severe carbon deposition due to metal stacking effects. Therefore, the layer double hydroxides (LDHs) were introduced into OC preparation to achieve uniform metal distribution and solve the above problems. Moreover, different enhanced OCs derived from LDHs precursors were prepared to investigate the effects of divalent metal, Ni/Fe (N/I), Methane/OCs (M/O) and reaction temperature, as well as the adaptability and performance of CL-SMR. The results showed that uniformly dispersed Ni–Fe–Al OC possessed promising CH 4 conversion of 94.32%, H 2 selectivity of 72.61%, CO selectivity of 77.46%, stability of syngas production with H 2 /CO ratio of 2 and low carbon deposition of 5.28%. Further, the increase of N/I from 0.5:2.5 to 2.5:0.5 caused an increase in CH 4 conversion, H 2 selectivity and CO selectivity by 95.04%, 598.82% and 68.19%, respectively. However, the highest N/I ratio led to severe carbon deposition (17.57%) in the Ni 2.5 Fe 0.5 Al OC. Furthermore, Ni–Fe–Al OC with uniformly dispersed active metal exhibited a good stability and suitability in wide-range of M/O and temperature. In addition, H 2 selectivity gradually improved with the increase of M/O, but higher M/O of 1.2 resulted in higher carbon deposition (7.99%). Further, the increase of temperature was beneficial to the OC performance, but excessive temperature (950 °C) led to OC sintering. Moreover, this Ni 2 FeAl OC maintained good catalytic ability and lattice oxygen stability after long-term reaction.
energy & fuels,electrochemistry,chemistry, physical