The effect of various Sn and Ca equal proportional addition on the microstructure, mechanical behavior and corrosion performance of Mg alloys
Pengfei Hua,Hui Zou,Yanfu Chai,Xinyu Chen,Huabao Yang,Yan Zhang,Chao He,Jun Xu,Yuhui Zhang,Bin Jiang
DOI: https://doi.org/10.1016/j.mtcomm.2024.110466
IF: 3.8
2024-12-01
Materials Today Communications
Abstract:In the present study, the effects of various Sn and Ca equal proportional addition (0.3:0.1, 0.6:0.2, 1.2:0.4, wt%) on the microstructure, mechanical properties and corrosion behavior of Mg-Sn-Ca alloys were systematically investigated. With the increase of Sn and Ca content, microstructure uniformity of the Mg-Sn-Ca alloy was improved, the average grain size was refined (from 34.4 μm to 21.62 μm, 13.47 μm), and more CaMgSn phases were generated (from 0.39 % to 1.64 %, 4.53 %). With increasing Sn and Ca content, the tensile yield strength (TYS) and ultimate tensile strength (UTS) of Mg-Sn-Ca alloys were gradually increased (TYS: from 91.8 MPa to 98.24 and 125.05 MPa; UTS: from 187.48 MPa to 190.73 and 214.58 MPa), mainly due to the contribution of grain refinement. The electrochemical tests revealed that the corrosion resistance of the Mg-Sn-Ca alloy initially decreases and then increases with the increase of Sn and Ca contents. The hydrogen evolution volume of Mg-0.3Sn-0.1Ca alloy was 41.91 mL cm−2, and the corrosion current density was −1.54 × 10−3 A/cm2. As for Mg-0.6Sn-0.2Ca alloy, deteriorated corrosion resistance compared to the Mg-0.3Sn-0.1Ca alloy was mainly ascribed to the micro-galvanic corrosion between the CaMgSn phase and Mg-matrix. The Mg-1.2Sn-0.4Ca alloy had the best corrosion resistance, with the lowest hydrogen evolution volume of 34.09 mL cm−2 and a minimum current density of −1.15×10−3 mA cm−2, its high corrosion resistance could be attributed to the grain refinement and homogenous distributed CaMgSn phase and more generated Ca(OH)2 product film with dense-structure.
materials science, multidisciplinary