Abstract:In the present study, the interstitial hydrogen (H) atoms were introduced as beta-stabilizing element to tailor the microstructure, martensitic phase transition, and functional properties of Ti-V-Al shape memory alloys for biomedical applications. The results revealed that the addition of interstitial H atoms into Ti-V-Al shape memory alloys induced the transition from a single alpha"" martensite to the coexistence of beta parent phase and alpha phase, regardless of H content. Moreover, the amount of alpha phase firstly increases and then decreases in the present Ti-V-Al based shape memory alloy with H content increasing. Besides, H addition resulted in larger lattice distortion, further causing the formation of nano-domains in Ti-V-Al based alloys. Besides, no endothermic and exothermic peaks were detected due to the confinement of alpha-phase, and the emergence of nano-domains. With increasing H atoms content, the mechanical properties such as fracture strength, hardness, recoverable strain for Ti-V-Al based shape memory alloys initially increased and then decreased. (Ti-13V-3Al)99.2H0.8 shape memory alloys exhibited the highest fracture strength of 862 MPa, superior hardness of 307HV, and the fully recoverable strain under 6% pre-strain as well as the moderate elastic modulus, which was mainly attributed to the solution strengthening of interstitial H atoms and the precipitation strengthening of alpha phase. The best corrosion resistance of Ti-V-Al based shape memory alloys was observed with the 2.0 at. % H, which was due to the formation of TiO2, Ti2O3 oxide films. Moreover, the best wear resistance with the lower wear rate of 0.9347 x 10-6 mm3/N mm was obtained in (Ti-13V-3Al)99 & sdot;2H0.8 shape memory alloy, due to the integrated effects of higher micro- hardness, reinforcing effect of alpha phase and lubrication effect of the hydrogenated film.

Corrosion and Wear Performance of Β-Ti Based Biomedical Shape Memory Alloys

A Comparative Study on Corrosion and Wear Performances of Ti–Nb–(Cu, Co) Biomedical Shape Memory Alloys

Corrosion resistance and cytocompatibility of Ti–19Zr–11Nb–4Ta shape memory alloy for biomedical applications

Comparative In Vitro Study of Ti-12V-9Sn Shape Memory Alloy with C.P. Ti and Ti-12V Alloy for Potential Biomedical Application

Microstructure and Mechanical Properties of Ti-Zr-Cr Biomedical Alloys.

Tribological Behaviour of Biomedical Ti–Zr-based Shape Memory Alloys

Tailoring Β-Ti Based Shape Memory Alloy with the Exceptional Mechanical and Functional Properties Towards Biomedical Bone Implants Application

Corrosion, Wear and Tribocorrosion Behavior of a New Biomedical Ti-20Zr-10Nb Alloy

The Microstructure Evolution, Wear and Corrosion Behavior of Biomedical Ti40Zr40Nb5Ta12Sn3 MEA at Different Heat Treatment Conditions

Development of Biomedical Ti-Nb-Zr-Mn Alloys with Enhanced Mechanical Properties and Corrosion Resistance

Tribocorrosion Behaviour of a Biomedical Ti-25Nb-3Mo-3Zr-2Sn Alloy in Ringer's Solution.

Impact of scandium on mechanical properties, corrosion behavior, friction and wear performance, and cytotoxicity of a β-type Ti–24Nb–38Zr–2Mo alloy for orthopedic applications

Ternary Ti-Zr-Nb and quaternary Ti-Zr-Nb-Ta shape memory alloys for biomedical applications: Structural features and cyclic mechanical properties

Sliding and Fretting Wear Behavior of Biomedical Ultrafine-Grained TiNbZrTaFe/Si Alloys in Simulated Physiological Solution

Synergistic Effect of TiN Ceramic Particle and Grain Refinement in Enhancing the Higher Performance Ti–V–Al Based Shape Memory Alloy

Investigation on Mechanical Compatibility Matching for Biomedical Titanium Alloys

Phase Constitution, Mechanical Property and Corrosion Resistance of the Ti-Nb Alloys

Mechanical, corrosion, and wear properties of biomedical Ti–Zr–Nb–Ta–Mo high entropy alloys

Wear characteristics of Ti–Nb–Ta–Zr and Ti–6Al–4V alloys for biomedical applications

Mechanical Properties and Corrosion Behavior of a Beta Titanium Alloy

Microstructure and Corrosion Resistance of Powder Metallurgical Ti-Nb-Zr-Mg Alloys with Low Modulus for Biomedical Application