Abstract:SiCf/SiC composite materials had become a research hotspot in the fields of aerospace materials and nuclear materials in recent years. This materials have high strength, radiation resistance, high temperature resistance and oxidation resistance. However, SiC is a typical brittle material prone to being damaged due to stress concentration in some cases, leading to cracks and even component failure. Therefore, this study employed an accurate and efficient numerical simulation method, phase field cohesive zone method (PFCZM), to investigate the microscopic damage behavior of SiCf/SiC composite materials. This study aimed to illustrate the influence of the thickness of pyrolytic carbon (PyC) interface layer on the failure behavior of SiCf/SiC composite materials. Firstly, this study conducted relevant verification of PFCZM. Secondly, numerical simulations of crack initiation, crack propagation, and final damage were performed by establishing a representative volume element (RVE). Observing the simulation results, it was noted that at low strain, when PyC was thicker, the SiCf/SiC composite materials exhibited slight damage to both the SiC matrix and PyC interface. Conversely, when PyC was thinner, the SiCf/SiC composite materials displayed only slight damage to PyC interface. As the PyC thickness increases, the damage to PyC interface decreases, while the damage to SiC becomes more prominent. Simultaneously, a competitive relationship in the damage behavior of SiCf/SiC composite materials can be found after the SiC matrix has cracked: When PyC is thinner, the damage primarily manifests as interlayer delamination between the SiC matrix and the SiC fiber. Conversely, when PyC is thicker, it manifests in PyC failure. Finally, this study concluded that, in this investigation, a PyC interface layer with a thickness of 0.1 μm exhibited the most effective protective effect on SiCf/SiC composite material.

Fracture Mechanical and Ablation Behaviors of C/SiC-Cu3Si-Cu Interpenetrating Composites and Their Dependence on Metal Addition and Interface Thickness

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

Interfacial Regulation and Fracture Mechanism of Al–Si/SiC Composites Infiltrated under Super-Gravity Field

Influence of Reinforcement with Multimodal Distribution on Thermophysical Properties and Fracture Behavior in Al-Si/SiC Composites Infiltrated under Super-Gravity Field

Mechanical Properties and Failure Behavior of 3D-SiCf/SiC Composites with Different Interphases

Microstructure, Mechanical and Ablation Properties of Transpiration Cooling Applied to C/C-SiC Composite for Novel Anti-ablation Material

Influences of fracture toughness and thermal conductivity on the ablation behavior of SiC-ZrC-MPCFs composite modified by mesophase-pitch-based carbon fibers

Construction of sandwich-structured C/C-SiC and C/C-SiC-ZrC composites with good mechanical and anti-ablation properties

Fracture Behaviour of SiCp/Al Composites with Network Architecture

Influence of thickness of pyrolytic carbon interphase on the mechanical behavior of SiC/(BN/PyC)/SiC composites

Microstructure characterization and fracture behaviors of Silicon carbide/metallic glass composites with interpenetrating architecture

Effect of PyC/BN interfacial phases on mechanical behavior of SiC/SiC composites

Investigation on crack propagation of SiCf/SiC composite via PF-CZM method

Mechanical and ablation properties of 3D orthogonal woven C/C-SiC composite based on high-solid-loading slurry impregnation

Effect of SiC on the anti-ablation resistance and flexural strength of (Hf-Ta-Zr)C-C/C composites

The oxide-layer configuration alteration and pseudo-ductile crack propagation mechanisms in composites induced by different relative thicknesses of CVI HfC-SiC multiphase matrix

Fracture toughness and progressive damage mechanisms of 2.5D woven SiCf/SiC composites

Damage Mechanism Analysis to the Carbon Fiber and Fiber-Ceramic Interface Tailoring of Cf/ZrC-SiC Using PyC Coating

Numerical Simulation of the Mechanical Properties and Fracture of SiCp/6061Al Composite Materials Based on Microstructure

Tunable strength of SiC<sub>f</sub>/-Yb<sub>2</sub>Si<sub>2</sub>O<sub>7</sub> interface for different requirements in SiC<sub>f</sub>/SiC CMC: Inspiration from model composite investigation

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy