Novel Positively Charged Metal-Coordinated Nanofiltration Membrane for Lithium Recovery
Li Wang,Danyal Rehman,Peng-Fei Sun,Akshay Deshmukh,Liyuan Zhang,Qi Han,Zhe Yang,Zhongying Wang,Hee-Deung Park,John H. Lienhard,Chuyang Y. Tang
DOI: https://doi.org/10.1021/acsami.1c02252
2021-04-02
Abstract:Nanofiltration (NF) with high water flux and precise separation performance with high Li<sup>+</sup>/Mg<sup>2+</sup> selectivity is ideal for lithium brine recovery. However, conventional polyamide-based commercial NF membranes are ineffective in lithium recovery processes due to their undesired Li<sup>+</sup>/Mg<sup>2+</sup> selectivity. In addition, they are constrained by the water permeance selectivity trade-off, which means that a highly permeable membrane often has lower selectivity. In this study, we developed a novel nonpolyamide NF membrane based on metal-coordinated structure, which exhibits simultaneously improved water permeance and Li<sup>+</sup>/Mg<sup>2+</sup> selectivity. Specifically, the optimized Cu–<i>m</i>-phenylenediamine (MPD) membrane demonstrated a high water permeance of 16.2 ± 2.7 LMH/bar and a high Li<sup>+</sup>/Mg<sup>2+</sup> selectivity of 8.0 ± 1.0, which surpassed the trade-off of permeance selectivity. Meanwhile, the existence of copper in the Cu–MPD membrane further enhanced anti-biofouling property and the metal-coordinated nanofiltration membrane possesses a pH-responsive property. Finally, a transport model based on the Nernst–Planck equations has been developed to fit the water flux and rejection of uncharged solutes to the experiments conducted. The model had a deviation below 2% for all experiments performed and suggested an average pore radius of 1.25 nm with a porosity of 21% for the Cu–MPD membrane. Overall, our study provides an exciting approach for fabricating a nonpolyamide high-performance nanofiltration membrane in the context of lithium recovery.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c02252?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c02252</a>.SEM images and photos of prepared membranes; ζ-potential of Cu–MPD NF membrane and PES substrate; AFM images of prepared membranes; XPS spectra and ζ-potential of prepared membranes; copper loading in the prepared membrane with different Cu/MPD ratios; UV–vis spectra and thickness of Cu–MPD oligomers with different Cu/MPD ratios; separation performance of membrane with different components; membrane anti-biofouling ability test by rotating disk; membrane anti-biofouling ability test by cross-flow filtration; copper leaching test in pure water; comparison of membrane filtration performance in this work to the literature; membrane long-term running stability test; feed, retentate, and permeate concentration in 12 h filtration; recipe for fabricating the Cu–MPD membrane; contact angle and isoelectrical point of prepared membranes; comparison of this work to the literature; Cu loading concentration in different types of membranes; average biofilm thickness and average biovolume on the surface of prepared membranes; I and Cu concentrations before and after 5 h reaction; performance of membrane with different recipes; and recipe of the membranes in Table S7 (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c02252/suppl_file/am1c02252_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology