A Comparative Study of Optical Properties and Temperature Sensing Characteristics of Ymo 4: Er 3+ (m=nb, Ta, V, P) Phosphors

Xin Wang,Xiangping Li,Yuhang Zhang,Baojiu Chen
DOI: https://doi.org/10.1016/j.inoche.2024.112812
IF: 3.428
2024-01-01
Inorganic Chemistry Communications
Abstract:In this work, the effects of M5+ ions on the optical properties and temperature sensing characteristics of YMO4: Er3+ (M = Nb, Ta, V, P) phosphors were considered in detail. YMO4 (M = Nb, Ta, V, P) with varied Er3+ concentrations were synthesized via a traditional solid-state reaction, and the crystal structure and phase purity were confirmed by means of X-ray diffraction. Upon the 980 nm excitation, Er3+ mainly exhibited green emission in YNbO4, YTaO4 and YVO4 samples, while YPO4: Er3+ sample mainly showed red emission. The upconversion (UC) mechanism was investigated by pump power dependence of emission spectra, and the green and red emission processes of Er3+ ions in YMO4 are 2-photon processes. Based on the Judd-Ofelt theory and diffuse reflection spectra, the oscillator strengths, transition rate, branch ratio and lifetime of Er3+ in YMO4 powder samples were calculated. Temperature sensing performances were estimated, and the obtained characteristics indicate that YNbO4: Er3+ shows the maximal temperature sensing sensitivity (0.0051 K-1), followed by YVO4: Er3+. According to the above results, the YNbO4: Er3+ phosphors are most promising for practical application in the field of optical temperature measurements.
What problem does this paper attempt to address?