Abstract:CoCrFeNiTi, a precipitation-strengthened high-entropy alloy (HEA), exhibits remarkable mechanical properties. Among its crucial secondary phases, the η phase holds significant importance. The CoCrFeNiTi HEA was fabricated using laser-directed energy deposition (LDED). The rapid non-equilibrium solidification process restricts the precipitation of the η phase. Utilizing the distinctive microstructure characteristics of LDED, the aging treatment was designed to promote the precipitation of two types of η phases. The η phase is primarily formed through a discontinuous precipitation reaction and exhibits a typical Blackburn orientation relationship with the matrix FCC phase: [1 ] FCC ‖ [2 ] η and (111) FCC ‖ (0001) η . At the L interface between the η phase and the FCC phase, the crystal planes are well-aligned and orderly, resulting in a coherent structure. However, at the W interface, the crystal planes are disordered, leading to an incoherent structure. This interface is clearly visible and is accompanied by a large number of crystal defects, such as dislocations and stacking faults. This unique interface structure significantly influences the nucleation, growth, and evolution of the η phase, further determining the overall microstructure and related properties of the HEA. The type 1 η phase appears blocky with an average size of ~ 920 nm and contains a higher proportion of W interfaces and stacking faults (SFs). Conversely, the type 2 η phase appears rodlike with an average size of ~ 375 nm and a high proportion of L interfaces. The nanohardness of type 1 η phase is 13.7 GPa, exhibiting inconsistent deformation behavior compared to the FCC phase matrix, such as the pop-in phenomenon. On the other hand, the nanohardness of type 2 η phase is 12.8 GPa, showing a better match with the matrix and playing a strong role in plastic equilibrium. By strategically designing the aging process and precisely controlling the morphology of the η phase, it becomes possible to facilitate the simultaneous proper precipitation of both types of η phase. This advancement contributes to enhancing the strength and promoting good plasticity of HEAs. This study offers an effective methodology for develop high-performance HEAs through microstructure and phase composition adjustments.

A Novel Strategy to Regulate the Precipitation-Strengthened High-Entropy Alloy Fabricated by Laser Directed Energy Deposition

Precipitation behaviors of the rapidly-solidified CoCrFeNiTi high-entropy alloy during aging treatment

Enhancing the Strength of AlCrFeNi HEAs Via Tailoring Aluminum Content and Optimal Aging Treatment

A new strategy to overcome the strength-ductility trade off of high entropy alloy

Two types of η phase synergistically improving the mechanical properties of LDED CoCrFeNiTi high-entropy alloy

Inhibiting cracking and improving strength for additive manufactured Al x CoCrFeNi high entropy alloy via changing crystal structure from BCC-to-FCC

Laser metal deposition of thin-walled parts of Al 0.8 CrFe 2 Ni 2 high-entropy alloy: Process window, microstructure, wear resistance and mechanical anisotropy

Strengthening and fracture mechanisms of a precipitation hardening high-entropy alloy fabricated by selective laser melting

Exceptional strength–ductility combination of CoCrFeMnNi high-entropy alloy with fully recrystallized structure by selective laser melting after post-deformation annealing

Superior Strength-Ductility Synergy in Additively Manufactured CoCrFeNi High-Entropy Alloys with Multi-Scale Hierarchical Microstructure

Strain hardening and strengthening mechanism of laser melting deposition (LMD) additively manufactured FeCoCrNiAl0.5 high-entropy alloy

Selective Laser Melting (SLM) Additively Manufactured CoCrFeNiMn High-Entropy Alloy: Process Optimization, Microscale Mechanical Mechanism, and High-Cycle Fatigue Behavior

Microstructures and precipitation behaviors of a hypoeutectic high-entropy alloy prepared by laser powder bed fusion

Additive manufacturing of Al0.3CoCrFeNi high-entropy alloy by powder feeding laser melting deposition

Control of Nanoscale Precipitation and Elimination of Intermediate-Temperature Embrittlement in Multicomponent High-Entropy Alloys

Achieving well-balanced strength and ductility via dual nanoscale precipitate structures in Co-free high-entropy alloys

Strength–Ductility Mechanism of CoCrFeMnNi High-Entropy Alloys with Inverse Gradient-Grained Structures

Simultaneously Enhanced Strength-Ductility of AlCoCrFeNi2.1 Eutectic High-Entropy Alloy Via Additive Manufacturing

Microstructure Evolution and Tensile Properties Behavior During Aging Temperature of Cocrfeni-Based High Entropy Alloys

Tuning of the Mechanical Properties of a Laser Powder Bed Fused Eutectic High Entropy Alloy Ni30Co30Cr10Fe10Al18W2 Through Heat Treatment

Microstructure, mechanical properties and corrosion resistance of direct energy deposited AlCu 0.25 CoCrFeNi 2.1 high entropy alloy: Tailored by annealing heat treatment