Abstract:As structural materials candidates of advanced fission and future fusion reactors, oxide-dispersion-strengthened (ODS) alloys, which are often ultrafine-grained (with a grain size between 100 and 1000 nm), have attracted widespread interest in past decades. However, fabrication of fully dense bulk nanocrystalline ODS alloys has rarely been reported. In this work, a novel Zr-doped nanocrystalline 14YWTZ ferritic ODS alloy (Fe-14Cr-3W0.4Ti-0.8Zr-0.3Y(2)O(3)) was prepared by mechanical alloying and high-pressure consolidation techniques. The high consolidation pressure (4 GPa) endows the bulk nanocrystalline 14YWTZ alloy with a nearly full relative density (similar to 99.5%) and a reasonable tensile elongation. The consolidated nanocrystalline 14YWTZ alloy with an average grain size of similar to 50 nm shows an ultra-high compressive yield strength of similar to 2641 MPa. Besides, the alloy exhibits an exceptional thermal stability, i.e., limited grain growth occurs after annealing at a high temperature of 1000 degrees C. After hot rolling, the alloy retains nanocrystalline microstructures and exhibits an unprecedented tensile yield strength of 2730 MPa, far exceeding those of previous reported ferritic ODS alloys. The high thermal stability of the annealed nanocrystalline 14YWTZ alloys can be ascribed to the combined effects of the thermodynamic multicomponent co-segregation to grain boundaries and strong kinetic Zener pinning by highdensity Zr-Ti-Y-O-enriched nanoparticles with an average particle size of similar to 3.18 nm and a high number density of similar to 3 x 10(24) m(3). The outstanding strength of the present nanocrystalline 14YWTZ alloys primarily originates from the Hall-Petch strengthening of the nanocrystalline matrix, distinguishing them from conventional ODS alloys strengthened by dislocation forest and/or dispersed oxide nanoparticles.

Processing Heterogeneously Structured Oxide-Dispersion-strengthened Fe-10Cr-6.1Al-0.3Zr-0.1Y Alloy for Simultaneously Enhanced Strength and Ductility

Mechanical Properties and Microstructure of 9Cr-Ods-clf-1 Steel

Microstructure Evolution and Mechanical Properties of ODS FeCrAl Alloys Fabricated by an Internal Oxidation Process

Enhanced strength-ductility combination by introducing bimodal grains structures in high-density oxide dispersion strengthened FeCrAl alloys fabricated by spark plasma sintering technology

Achieving ultrahigh strength in oxide-dispersion-strengthened CoCrNi alloy via in situ formation of coherent Y-Ti-O nanoprecipitates

Achieving high strength and ductility in ODS-W alloy by employing oxide@W core-shell nanopowder as precursor

Optimization of Microstructure and Tensile Properties for a 13Cr-1W ODS Steel Prepared by Mechanical Alloying and Spark Plasma Sintering Using Pre-Alloyed Powder

Characterization of Oxide Dispersoids and Mechanical Properties of 14Cr-Ods FeCrAl Alloys

Fabrication of Oxide-Dispersion-Strengthened Ferritic Alloys by Mechanical Alloying Using Pre-Alloyed Powder

Development of Oxide Dispersion Strengthened Ferritic Steel with Enhanced Strength–ductility Combination Through Dispersion Strengthening and Back Stress Hardening

Combination of Back Stress Strengthening and Orowan Strengthening in Bimodal Structured Fe–9Cr–Al ODS Steel with High Al Addition

Ultrastrong Nanocrystalline Oxide-Dispersion-strengthened Ferritic Alloy with Exceptional Thermal Stability

Characterization of oxide dispersion strengthened ferritic steel fabricated by electron beam selective melting

Basic Characterization of Oxide Dispersion Strengthened Fine-Grained Tungsten Based Materials Fabricated by Mechanical Alloying and Spark Plasma Sintering

Microstructure and properties of oxide-reinforced FeCrAl matrix alloy manufactured by selective laser melting

Additive manufactured oxide-dispersion strengthened FeCrNi medium entropy alloy with superior mechanical properties

Influence of Yh2 Nanoparticles Addition on the Microstructure and Mechanical Properties of Oxide Dispersion Strengthened Ferritic Alloys

Effect of Fe2O3 additive on microstructure and high temperature tensile properties of oxide dispersion-strengthened Fe12CrWTiY alloys

Feasibility of using Y 2 Ti 2 O 7 nanoparticles to fabricate high strength oxide dispersion strengthened Fe–Cr–Al steels

Superior strength-ductility synergy of an oxide-dispersion strengthened CoCrNi-based multi-principal element alloy

Influence of Al Addition Strategy on the Microstructure of a Low‐Cr Oxide Dispersion‐Strengthened Ferritic Steel