Abstract:: In order to improve the early age strength of ordinary Portland cement-based materials, many early strength agents were applied in di ﬀ erent conditions. Di ﬀ erent from previous research, the nano calcium silicate hydrate (C-S-H) particles used in this study were synthesized through the chemical reaction of CaO, SiO 2 , and H 2 O under 120 ◦ C using the hydrothermal method, and the prepared nano C-S-H particles were highly crystalized. The inﬂuences of di ﬀ erent amounts of nano C-S-H particles (0%, 0.5%, 1%, 2% and 3% by weight of cement) on the setting time, compressive strength, and hydration heat of cement paste were studied. The hydration products and microstructure of the cement paste with di ﬀ erent additions of nano C-S-H particles were investigated through thermogravimetry-di ﬀ erential thermal analysis (TG-DTA), X-ray powder di ﬀ raction (XRD), and scanning electron microscope (SEM) tests. The results show that the nano C-S-H particles could be used as an early strength agent, and the early strength of cement paste can be increased by up to 43% through accelerating the hydration of tricalcium silicate (C 3 S). However, the addition of more than 2% nano C-S-H particles was unfavorable to the later strength development due to more space being left during the initial accelerated hydration process. It is suggested that the suitable content of the nano C-S-H particles is 0.5% − 1% by weight of cement. 1%, 2%, and 3% nano C-S-H 1.87%, 1.98%, 2.07%, 1.94%, and 1.98%, respectively. At the age of 28 days, the losses at the location of the first peak (4.6%) location of Ca(OH) 2 (2.0%) were almost the same for different paste samples, that their TG curves were similar to each other. The loss rate in curves is consistent with that in the DTA diagram. These results show that at the early ages (1 and 7 days), the C-S-H particles the formation of Ca(OH) 2 , which is the hydration product from C 3 S at early age. As it is that the formation of Ca(OH) is associated with the new C-S-H the nano C-S-H particles also the formation of C-S-H gel. At the age (28 days), the effect of nano C-S-H particles on the hydration products is not very significant. From the compressive strength results at 28 days, the different strength the of the hydration methodology, J.W. and Y.W.; formal analysis, Y.W., H.H. and H.L.; investigation, H.L. and H.H.; writing—original draft preparation, H.L., J.W. and Y.W.; writing—review and editing, J.W. and Y.W.; supervision, J.W. and Y.W.; project administration, J.W. and Y.W.; funding acquisition, Y.W.

Effect of Microscale C–S–H on the Properties of Portland Cement and Hydration Kinetics Analysis at Different Curing Temperatures

Preparation of Nano-Sized C-S-H and Its Acceleration Mechanism on Portland Cement Hydration at Different Temperatures

Effect of n-C-S-H on Hydration and Reinforcement of Mineral Powder-Cement System at Low Temperatures

Insight into the local C-S-H structure and its evolution mechanism controlled by curing regime and Ca/Si ratio

Effects of Highly Crystalized Nano C-S-H Particles on Performances of Portland Cement Paste and Its Mechanism

Influence of Curing Temperature on the Performance of Calcined Coal Gangue-Limestone Blended Cements

E ﬀ ects of Highly Crystalized Nano C-S-H Particles on Performances of Portland Cement Paste and Its Mechanism

Effect of Curing Temperature on Mechanical Strength and Thermal Properties of Hydraulic Limestone Powder Concrete

Improving the Mechanical Properties of Cement-Based Materials under High Temperature: Reducing the C3s/C2s Ratio

The Effect of Curing Regimes on the Mechanical Properties, Nano-Mechanical Properties and Microstructure of Ultra-High Performance Concrete

Effect of Calcium Silicate Hydrate Seeds on Hydration and Mechanical Properties of Cement

Experimental study of pure Class G cement hydration up to 150oC and 50MPa

Effects of Nano-CSH on the hydration process and mechanical property of cementitious materials

Experimental Study of Pure Class G Cement Hydration Up to 150 °C and 50 MPa

Study On Effect Of Carbonation Curing For Cement Minerals And Clinker

Effect of Chlorine Salt Content on the Microstructural Development of C-S-H Gels and Ca(OH)2 at Different Curing Temperatures

The Influence of Inorganic Admixtures on Early Cement Hydration from the Point of View of Thermodynamics

Hydration Kinetics of Cement Composites with Different Admixtures at Low Temperatures

Temperature Effect of Hydration and Microstructure of Tricalcium Silicate–Slag Powder Hydrated Composites: An Experimental and Molecular Dynamics Investigation

Effect of curing regimes on strength of magnesium silicate hydrate cement

Temperature-Dependent Hydration and Mechanical Properties of High-Volume Fly Ash Cement with Chemical Additives