Effect of Pre-Welding Pulse on Microstructure and Mechanical Properties for Parallel Gap Resistance Welding Joint of GaAs Solar Cell and Ag Foil

Yuhan Ding,Zhichao Wang,Xiaoran Li,Yi Wei,Chen Shen,Xueming Hua,Min Wang,Lin Wang,Bin Qian

DOI: https://doi.org/10.1109/icept59018.2023.10492001

2023-01-01

Abstract:Bonding strength of Ag foil and electrode of solar cell has a significant influence on the service life of solar cell panels in space environment. Although it is known that increasing the welding energy via changing welding parameters can improve bonding strength of parallel gap resistance welding (PGRW) joints, excessive welding energy for solar cell interconnection would lead to fragmentation or degradation of electrical properties of solar cell. The multi-pulse welding method can reduce instantaneous current and increase the total welding energy during PGRW process. Therefore, it is of great significance to elucidate the effect of pre-welding pulse on PGRW process to improve welding quality. In the present research, interconnection of GaAs space solar cell and Ag foil are achieved by PGRW processes with various pre-welding pulses. Firstly, the surface condition of Ag foil and Au layer of GaAs solar cell was characterized by atomic force microscope (AFM). Subsequently, the morphology of the zone objected different pre-welding pulses was investigated by scanning electron microscope (SEM). It is found that the surface roughness has a vital effect on welding energy in micro-leveled interconnection. The results of tensile-shear test shows that the tensile-shear force increases with the increase of pre-welding voltage. Combined with the cross-section SEM images of joints and the simulation of PGRW process, The pre-welding pulse can increase the bonding region via enhanced the total welding energy. Although the pre-welding pulse can reduce the surface roughness, the improvement of stability and welding energy of PGRW process provides better joints of solar cell. In addition, joints with a solid-phase diffusion interface optimized by a 0.3V pre-welding voltage shows better and stabler tensile-shear force.