Electrochemical Behavior and Discharge Performance of Al-1zn-0.4mn-0.1sn-Xbi As Anode Alloys for Al-Air Battery in Koh Solution

Jingong Qin,Lei Li,Yanling Tu,Fanglin Cao,Yusong Suo,Xiangjie Wang,Jianzhong Cui

DOI: https://doi.org/10.1016/j.matchemphys.2024.130200

IF: 4.778

2024-01-01

Materials Chemistry and Physics

Abstract:Al-1Zn-0.4Mn-0.1Sn-xBi (x = 0, 0.5, 0.10, 0.15, 0.20) alloys are prepared as anode materials in alkaline Al-air batteries by adding alloying elements to low-cost commercial purity aluminum to investigate their electrochemical behavior and discharge performance. The results show that among the five alloys, Al-1Zn-0.4Mn-0.1Sn-0.15Bi alloy has the best comprehensive corrosion resistance and discharge performance in 4M KOH electrolyte at room temperature. Specifically, Al-1Zn-0.4Mn-0.1Sn-0.15Bi has the most negative corrosion potential of -1.484 V and the smallest corrosion current density of 42.80 mA cm-2, which can be attributed to the largest protective film impedance. The hydrogen evolution rate of this alloy is as low as 0.244 ml cm-2 min-1. Upon discharge at a current density of 60 mA cm-2, this anode alloy achieves an anode efficiency of 89.20% and a specific capacity of 2656 Ah kg-1. Furthermore, when the discharge current density is further increased to 90 mA cm-2, it can still maintain a stable discharge at a high cell voltage of 1.01V, and the power density reaches 90.9 mW cm-2. Therefore, Al-1Zn-0.4Mn-0.1Sn-0.15Bi can be considered as a suitable anode alloy for high-power-density discharge in Al-air batteries.