Fatigue Damage Tolerance of CFRP/Al Adhesive Joints with Thermal Effects

Zongkai He,Gang Zheng,Quantian Luo,Qing Li,Guangyong Sun
DOI: https://doi.org/10.1016/j.ijmecsci.2024.109543
IF: 7.3
2024-01-01
International Journal of Mechanical Sciences
Abstract:In order to promote application of adhesive connection in primary load-bearing structures for engineering practice, tolerance of fatigue damage signifies a critical parameter in line with the guidance of FAA AC 20-107B. This study aims to investigate this issue from four aspects, namely, statistics of fatigue cracks, residual performance, critical point for fatigue damage tolerance, and degradation of adhesive property. To carry out a dedicated study, the carbon fiber reinforced polymer and aluminum (CFRP/Al) adhesive joint specimens with different degrees of fatigue damage were considered by monitoring real-time variation of stiffness in the course of pre-fatigue loading. The residual strengths at different temperatures and related degradation mechanisms were explored through the experimental tests and numerical analysis. The study suggests the 92% normalized stiffness to be a critical point, at which the structural safety factor is 2.5. It is found that a safety factor of 1.5 may not be sufficient for the structure under fatigue condition as the joint is fairly susceptible in the structure. This study unveiled that a reliable management for residual fatigue performance can be achieved. It is anticipated to provide an effective guide for damage-tolerant design, reliable safety monitoring, and punctual repair of damaged adhesive structure.
What problem does this paper attempt to address?