Influence of MoSi2 on oxidation protective ability of TaB2-SiC coating in oxygen-containing environments within a broad temperature range
Xuanru Ren,Junshuai Lv,Wei Li,Yuwen Hu,Ke Sun,Can Ma,Hong’ao Chu,Weiguang Wang,Leihua Xu,Ziyu Li,Peizhong Feng
DOI: https://doi.org/10.1007/s40145-020-0406-5
IF: 11.534
2020-08-13
Journal of Advanced Ceramics
Abstract:Abstract TaB 2 -SiC coating modified by different content of MoSi 2 was fabricated on graphite substrate with SiC inner coating by liquid phase sintering to elevate the anti-oxidation capability of the TaB 2 -SiC coatings. As compared to the sample with the TaB 2 —40wt%SiC coating, the coating sample modified with MoSi 2 exhibited a weight gain trend at lower temperatures, the fastest weight loss rate went down by 76%, and the relative oxygen permeability value reduced from about 1% to near 0. More importantly, the large amount of SiO 2 glass phase produced over the coating during oxidation was in contact with the modification of MoSi 2 , which was proved to be beneficial to the dispersion of Ta-oxides. A concomitantly formed continuous Ta-Si-O-B compound glass layer showed excellent capacity to prevent oxygen penetration. However, when the TaB 2 content was sacrificed to increase the MoSi 2 content, the relative oxygen permeability of the coating increased instead of decreased. Thus, on the basis of ample TaB 2 content, increasing the MoSi 2 content of the coating is conducive to reducing the relative oxygen permeability of the coatings in a broad temperature region.
materials science, ceramics