Fabrication and characterization of polyphenylene sulfide composites with ultra-high content of carbon fiber fabrics
Liang Zhao,Qizhong Ge,Jiuxiao Sun,Jiashun Peng,Xianze Yin,Leping Huang,Jihui Wang,Hua Wang,Luoxin Wang
DOI: https://doi.org/10.1007/s42114-019-00111-w
IF: 11.806
2019-08-16
Advanced Composites and Hybrid Materials
Abstract:In this study, polyphenylene sulfide (PPS) composite, which has ultra-high content of carbon fiber fabrics (CFF), was prepared from CFF and PPS nonwoven by a facile thermal-compressive method. The results show that the PPS composite composed of 80 wt% CFFs has optimal mechanical properties, where the tensile strength, fracture elongation, elastic modulus, flexural strength, flexural modulus, interlaminar shear strength, and impact strength reach to 1200.3 MPa, 20.3%, 25.7 GPa, 1305.6 MPa, 230.6 GPa, 110.3 MPa, and 348.6 KJ/m2, respectively. In addition, the volume resistivity, conductivity, and surface resistivity of the PPS composite with 80 wt% CFFs can reach to 1.3 × 10−2 Ω·cm, 74.9 S/cm, and 1.2 × 10−1 Ω·□ respectively. The increased interfacial layer and riveting effect between CFFs are responsible for outstanding structural stability and stress transformation, resulting in ultra-high strength and modulus of CFF/PPS composite, as well as the conductive performance.Graphical abstractSchematic diagram of failure mechanism and optical microscope images of cross sections of CFF/PPS composites.
nanoscience & nanotechnology,materials science, composites