Effect of Al(OH) 3 on Sintering Properties and Thermal Shock Resistance of Yttrium Oxide Materials

Yuan Chen,Yaowu Wei,Yiming Yu,Yale Liu,Bo Chen,Kui Liu

DOI: https://doi.org/10.1007/s10853-024-09449-z

IF: 4.5

2024-01-01

Journal of Materials Science

Abstract:Y 2 O 3 materials have been widely applicated in high temperature industry owing to its high temperature stability. However, the poor sintering behavior and thermal shock resistance limited its application. The existing studies were focused on its sintering properties, yet the increase in densification of Y 2 O 3 materials could weaken its thermal shock resistance. Y 2 O 3 materials with smaller closed pores were fabricated by the decomposition of Al(OH) 3 and the effect of Al(OH) 3 on the microstructure, mechanical properties and thermal properties of Y 2 O 3 materials were investigated in this paper. We concluded that the migration of grain boundaries was accelerated due to the ionic radii difference and the diffusion coefficient between Y 3+ and Al 3+ , and the diffusion coefficient of Y 3+ was relatively weak while the diffusion of Al 3+ was mainly dominated. The Al 2 O 3 produced by decomposition of Al(OH) 3 was active, which promoted the sintering of Y 2 O 3 materials. Meanwhile, the porosity and pore structure of Y 2 O 3 materials were affected by the decomposition of Al(OH) 3 , and the appropriate pores improved the thermal shock resistance by absorbing thermal stresses. Furthermore, it indicated that adding Al(OH) 3 into Y 2 O 3 materials had a powerful influence in balancing its sintering properties and thermal shock resistance. The sample with 3 wt% Al(OH) 3 exhibited the better performance in this study, with the relative density of 93.2% and the thermal shock stability factor parameter R st of 1.74 W m 1/2 .