Abstract:Novel high quality factor microwave dielectric ceramics (1-x)ZrTiO4-x(Mg1/3Nb2/3)TiO4 (0.325x0.4) and (ZrTi)(1-y)(Mg1/3Nb2/3)(y)O-4 (0.2y0.5) with the addition of 0.5wt% MnCO3 in the (Mg1/3Nb2/3)O-2-ZrO2-TiO2 ternary system were prepared, using solid-state reaction method. The relationship between the structure and microwave dielectric properties of the ceramics was studied. The XRD patterns of the sintered samples reveal the main phase belonged to -PbO2-type structure. Raman spectroscopy and infrared reflectivity (IR) spectra were employed to evaluate phonon modes of ceramics. The 0.65ZrTiO(4)-0.35(Mg1/3Nb2/3)TiO4-0.5wt% MnCO3 ceramic can be well densified at 1240 degrees C for 2hours and exhibits good microwave dielectric properties with a relative permittivity (epsilon(r)) of 42.5, a quality factor (Qxf) value of 43520GHz (at 5.9Ghz) and temperature coefficient of resonant frequency ((f)) value of -5ppm/degrees C. Furthermore, the (ZrTi)(0.7)(Mg1/3Nb2/3)(0.3)O-4-0.5wt% MnCO3 ceramic sintered at 1260 degrees C for 2hours possesses a epsilon(r) of 31.8, a Qxf value of 35640GHz (at 6.3GHz) and a near zero (f) value of -5.9ppm/degrees C. The results demonstrated that the (Mg1/3Nb2/3)O-2-ZrO2-TiO2 ternary system with excellent properties was a promising material for microwave electronic device applications.

Dielectric Properties of Zirconium Tin Titanate with Additives of ZnO, CuO, MnCO<sub>3</sub> and Bi<sub>2</sub>O<sub>3</sub>

Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics

High quality factor microwave dielectric ceramics in the (Mg1/3Nb2/3)O2–ZrO2–TiO2 ternary system

Effects of CuO-V<sub>2</sub>O<sub>5</sub>-Bi<sub>2</sub>O<sub>3</sub> Additions on the Microstructure and Microwave Dielectric Properties of 0.42ZnNb<sub>2</sub>O<sub>6</sub>-0.58TiO<sub>2</sub> Ceramics

Effect of Zn0·17Nb0·33Ti0·5O2 on the Microwave Dielectric Properties of ZnTiNb2O8 Ceramics

Effect of TiO2 Content on the Microwave Dielectric Properties of BaO-ZnO-TiO2 Ceramics

Low Temperature Sintering and Microwave Dielectric Properties of (zn0.65mg0.35)tio3 Ceramics with BiVO4

Preparation and Characterization of (Co0.3zn0.7)(ti1-Xsnx)nb2o8 Microwave Dielectric Ceramics

Co 2 O 3 substitution effects on the structure and microwave dielectric properties of low-firing (Zn 0.9 Mg 0.1 )TiO 3 ceramics

Effects of Ti<sup>4+</sup> Substitution on Microstructure and Microwave Dielectric Properties of ZnNb<sub>2(1-x)</sub>TixO<sub>(6-3x)</sub> Ceramics

Composite Dielectrics (1−x)(mg0.97zn0.03)2(ti0.95sn0.05)o4−xcatio3 Suitable for Microwave Applications

Low Temperature Sintering and Microwave Dielectric Properties of Zr 0.3 (zn 1/3 Nb 2/3 ) 0.7 TiO 4 Ceramics Doped with CuO-B 2 O 3

Preparation and characterization of (Co<sub>0:3</sub>Zn<sub>0:7</sub>)(Ti<sub>1–x</sub>Sn<sub>x</sub>)Nb<sub>2</sub>O<sub>8</sub> microwave dielectric ceramics

Influence of Zn0.5Ti0.5NbO4 on the Structure and Microwave Dielectric Properties of ZrTiO4 Ceramics

The Effect of Mn Addition on Phase Development, Microstructure and Microwave Dielectric Properties of ZrTi2O6–ZnNb2O6 Ceramics

Low temperature sintering and microwave dielectric properties of (Zn 0.65 Mg 0.35 )TiO 3 ceramics with BiVO 4

Microwave Dielectric Properties of ZnO-2TiO 2 -Nb 2 O 5 Ceramics with BaCu (B 2 O 5 ) Addition

Structure and Microwave Dielectric Properties of (zn1/3nb2/3)4+ Co-Substituted MgTiO3 Ceramic

Effect of ZnO Ratio on Sintering Behavior and Microwave Dielectric Properties of BaO–ZnO–TiO2 Ceramics

Low-fired microwave dielectrics in ZnO-TiO 2 ceramics doped with CuO and B 2 O 3

Dielectric Properties of Zirconium Tin Titanate with Additives of ZnO, CuO, MnCO&lt;sub&gt;3&lt;/sub&gt; and Bi&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;3&lt;/sub&gt;