Abstract:Controlled synthesis of carbon nanotubes (CNTs) and assembling them into macroscopic structures are of great importance to the applications of carbon nanotubes, and a deep understanding of the growth mechanism of carbon nanotubes would be an indispensable prerequisite for well-defined synthesis in a controllable way. Here we show some of our recent progress in carbon nanotube's growth mechanism, controlled synthesis, and applications. By introducing a ~ 13C labeling method, we revealed that the growth mechanism of the carbon nanotubes made by chemical vapor deposition (CVD) is the “extrusion model”. Serials of labels can be embedded into CNTs by tuning the composition and the flow rate of the reactive gases during the growth process, and the growth rate of CNT arrays can be calculated thereby. The fabrication of super\|aligned CNT arrays was expanded to 4-inch wafer scale. A novel method was invented to process the raw yarn by passing through volatile organic solvents. As a result, both the strength and manipulability were improved substantially. The processed yarn can be applied as thermal electron sources, large current density field emitters and in fluorescent tubes etc. Thermal interface materials (TIMs) has significant importance in IT industry, we prepared CNT array-polymer matrix which has very high thermal conductivity and extremely low thermal resistance. Techniques like chemical modification, tip etching and surface metal layer were explored to enhance the thermal conductivity of the CNT thermal interface materials.

Direct Synthesis of Ultralong Carbon Nanotube Bundles by Spray Pyrolysis and Investigation of Growth Mechanism

Synthesis of Ultralong Carbon Nanotubes with Ultrahigh Yields.

Direct Synthesis of Long Single-Walled Carbon Nanotube Strands.

Rapid Growth of Well-Aligned Carbon Nanotube Arrays

Growth of High-Density Parallel Arrays of Ultralong Carbon Nanotubes with Catalysts Pinned by Silica Nanospheres

Fabrication of Ultralong and Electrically Uniform Single-Walled Carbon Nanotubes on Clean Substrates

Synthesis Of Large Quantity Single-Walled Carbon Nanotubes By Arc Discharge

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

Production Of Large Area Carbon Nanotube Bundles On Metal Substrate

TEM Investigation on the Growth Mechanism of Carbon Nanotubes Synthesized by Hot-Filament Chemical Vapor Deposition.

Large-Scale and Selective Synthesis of Carbon Nanofiber Bundles, Curved Carbon Nanofibers and Helical Carbon Nanofibers.

Single Walled 0.4 Nm Carbon Nanotube Bundles Prepared By Pyrolysis Of N-Hexane Catalyzed By Ferrocene

Explorations on growth mechanism, controlled synthesis and applications of carbon nanotubes

High Yield Synthesis and Growth Mechanism of Carbon Nanotubes

The Fabrication of Macroscopical Long Aligned Carbon Nanotube Arrays

Long Bundles of Aligned Carbon Nanofibers Obtained by Vertical Floating Catalyst Method

Aerosol synthesis of single-walled carbon nanotubes by tuning feeding flow configuration for transparent conducting films

High-Strength Carbon Nanotube Fibers from Purity Control by Atomized Catalytic Pyrolysis and Alignment Improvement by Continuous Large Prestraining

Floating Bimetallic Catalysts for Growing 30 cm‐Long Carbon Nanotube Arrays with High Yields and Uniformity

Correction to Growth of Half-Meter Long Carbon Nanotubes Based on Schulz–Flory Distribution

Film growth of pillars of multi-walled carbon nanotubes