Cobalt Surface Modification During Γ-Fe2o3 Nanoparticle Synthesis by Chemical-Induced Transition

Junming Li,Jian Li,Longlong Chen,Yueqiang Lin,Xiaodong Liu,Xiaomin Gong,Decai Li
DOI: https://doi.org/10.1016/j.matchemphys.2014.11.022
IF: 4.778
2015-01-01
Materials Chemistry and Physics
Abstract:In the chemical-induced transition of FeCl2 solution, the FeOOH/Mg(OH)2 precursor was transformed into spinel structured γ-Fe2O3 crystallites, coated with a FeCl3·6H2O layer. CoCl2 surface modified γ-Fe2O3 nanoparticles were prepared by adding Co(NO3)2 during the synthesis. CoFe2O4 modified γ-Fe2O3 nanoparticles were prepared by adding NaOH during the surface modification with Co(NO3)2. The CoFe2O4 layer grew epitaxially on the γ-Fe2O3 crystallite to form a composite crystallite, which was coated by CoCl2·6H2O. The composite could not be distinguished using X-ray diffraction or transmission electron microscopy, since CoFe2O4 and γ-Fe2O3 possess similar spinel structures and lattice constants. X-ray photoelectron spectroscopy was used to distinguish them. The saturation magnetization and coercivity of the spinel structured γ-Fe2O3-based nanoparticles were related to the grain size.
What problem does this paper attempt to address?