Synthesis, microstructure, and magnetic properties of gamma-Fe2O3/NiO core/shell nanoflowers
Li Zhi-Wen,He Xue-Min,Yan Shi-Ming,Song Xue-Yin,Qiao Wen,Zhang Xing,Zhong Wei,Du You-Wei
DOI: https://doi.org/10.7498/aps.65.147101
IF: 0.906
2016-01-01
Acta Physica Sinica
Abstract:The main purpose of this work is to explore the influences of microstructures on the magnetic properties, as well as the formation mechanism of gamma-Fe2O3/NiO core/shell nanoflowers. The synthesis of nanoflower-like samples includes three processes. Firstly, Fe3O4 nanospheres are synthesized by the solvothermal reaction of FeCl3 dissolved in ethylene glycol and NaAc. Secondly, Fe3O4/Ni(OH)(2) core/shell precursor is fabricated by solvothermal method through using the early Fe3O4 spheres and Ni(NO3)(2)center dot 6H(2)O in an ethanol solution. Finally, the precursor Fe3O4/Ni(OH)(2) is calcined in air at 300 degrees C for 3-6 h, and therefore resulting in gamma-Fe2O3/NiO core/shell nanoflowers. Their microstructures are characterized by using XRD, XPS, SEM, HRTEM and SAED techniques. The results show that the final powder samples are gamma-Fe2O3/NiO with typical core/shell structure. In this core/shell system, the gamma-Fe2O3 sphere acts as core and the NiO acts as shell, which are comprised of many irregular flake-like nanosheets with monocrystalline structure, and these nanosheets are packed together on the surfaces of gamma-Fe2O3 spheres. The calcination time of Fe3O4/Ni(OH)(2) precursor has significant influences on the grain growth, the NiO content and the compactness of NiO shells in the gamma-Fe2O3/NiO core/shell system. VSM and SQUID are used to characterize the magnetic properties of gamma-Fe2O3/NiO core/shell nanoflowers. The results indicate that the 3 h-calcined sample displays better ferromagnetic properties (such as higher M-s and smaller H-C) because of their high gamma-Fe2O3 content. In addition, as the coupling interaction between the FM gamma-Fe2O3 and AFM NiO components, we observe that the gamma-Fe2O3/NiO samples formed in 3 h and 6 h display certain exchange bias (H-E = 20 and 46 Oe, respectively). Such a coupling effect allows a variety of reversal paths for the spins upon cycling the applied field, and thereby resulting in the enhancement of coercivity (H-C (FC) = 252 and 288 Oe, respectively). Further, the values of H-E and H-C for the former are smaller than those of the latter, this is because of the AFM NiO content in 6 h-calcined sample much higher than that in 3 h-calcined sample. Especially, the temperature dependences of the magnetization M of the two samples under both ZFC and FC conditions indicate that an extra anisotropy is induced. In a word, the size effect, NiO phase content, and FM-AFM (where FM denotes the ferromagnetic gamma-Fe2O3 component, while AFM is the antiferromagnetic NiO component) interface coupling effect have significant influence on the magnetic properties of gamma-Fe2O3/NiO core/shell nanoflowers.