Abstract:This work investigates the effect of adding SiC nanowires (SiCNWs) on the microstructure and mechanical properties of Mg-2Zn-0.1Y matrix composites under different hot extrusion parameters, and the strengthening mechanism was analyzed. The results showed that as the extrusion temperature elevated from 140 °C to 220 °C or the extrusion speed increased from 0.1 mm/s to 1.0 mm/s, both the dynamic recrystallized grain size and the recrystallized volume fraction increased significantly. The changes of precipitate size and volume fraction exhibited the same trend. The finest recrystallized grains (~0.37 μm) were obtained after extrusion at 140 °C and 0.1 mm/s, which also contained nano-sized MgZn2 precipitates and SiC nanowires. As the extrusion temperature increased from 140 °C to 220 °C at a constant extrusion speed of 0.1 mm/s, the strength of the composites decreased while the elongation improved greatly. Similar change in the strength and elongation were obtained in the composite as the extrusion speed increased from 0.1 mm/s to 1.0 mm/s at extrusion temperature of 140 °C. Meanwhile, these composites exhibited a weakened texture, and a mixture of microcracks and dimples was observed in the fracture surfaces of the as-extruded composites, which explained the mix of brittle-ductile fractures of the composites. The composites extruded at 140 °C and 0.1 mm/s exhibited the best performance with yield strength (YS) and ultimate tensile strength (UTS) of ~495.53 MPa and ~514.18 MPa, respectively. Among all strengthening mechanisms, the proportion of grain refinement strengthening is the highest.

Study of the Micro-Yielding Behavior in a SiCp/Mg–Zn–Ca Composite Using Synchrotron Radiation Diffraction

Study on the Mechanical Property of High‐Performance Silicon Carbide Fiber

Fracture Mechanism of Nano- and Submicron-Sicp/mg Composite During Room Temperature Tensile Test: Interaction Between Double Sized Particles and Dislocations

Microstructure and Elevated Tensile Properties of Submicron SiCp/AZ91 Magnesium Matrix Composite

Experimental and Numerical Investigations of Tensile Properties of SiC Particle‐Reinforced Composites

Microstructure, Texture and Mechanical Properties of Mg-2.10Zn-0.58Ca-1.02Zr-10.34SiCp (wt%) Composites after Being Extruded at Different Speeds

Studies on Microyield Behavior of Sicp/2024al Composite Materials

Effect of hot extrusion on the microstructure and mechanical properties of SiCNWs/Mg-2Zn-0.1Y composite

Numerical Simulation of the Mechanical Properties and Fracture of SiCp/6061Al Composite Materials Based on Microstructure

Microstructures, Interface Structure and Room Temperature Tensile Properties of Magnesium Materials Reinforced by High Content Submicron SiCp

Microstructure and Tensile Properties of Magnesium Matrix Composite: Effected by Volume Fraction of Micron Sicp

Microstructure and fracture behaviour of ZrO2 (2 mol% Y2O3) reinforced with SiC whiskers

Study on Behavior of Dynamic Fracture in SiC Nanoparticles Reinforced Magnesium Matrix Composites

Study on Fracture Behavior of Particulate Reinforced Magnesium Matrix Composite Using in Situ SEM

Microstructure and room temperature tensile properties of 1 μm-SiCp/AZ31B magnesium matrix composite

Determination for the Yield Strength of Matrix in a SiCw/Al Composite by the X-ray Diffraction

Microstructure And Fracture Behaviour Of Zro2 (2 Mol% Y2o3o) Reinforced With Sic Whiskers

In Situ X-ray Imaging and Numerical Modeling of Damage Accumulation in C/SiC Composites at Temperatures Up to 1200 ℃

Investigation on microstructure control of in-situ synthesized high-performance Cf/SiC composites

The deformation and fracture behavior of SiCw/AZ91 magnesium matrix composite during in-situ TEM straining

Microstructure and mechanical properties of SiC reinforced AlSi10Mg composites fabricated by laser metal deposition