Microstructure, Texture and Mechanical Properties of Mg-2.10Zn-0.58Ca-1.02Zr-10.34SiCp (wt%) Composites after Being Extruded at Different Speeds

Yanping Wang,Xihai Li,Hong Yan,Boyu Liu,Zhiwei Shan,Rongshi Chen

DOI: https://doi.org/10.1016/j.jallcom.2024.177688

IF: 6.2

2024-01-01

Journal of Alloys and Compounds

Abstract:The Mg-2.10Zn-0.58Ca-1.02Zr-10.34SiCp (wt%, SiCp/ZX20K) composites were fabricated by stir casting and hot extruded at 400 °C with extrusion speed of 5mm/s and 10mm/s, respectively. The SiC particles, which initially exhibited a necklace-type distribution at the grain boundaries, transformed into a band-type distribution after hot extrusion. The SiCp/ZX20K composites underwent complete recrystallization, resulting in a pronounced bimodal microstructure consisting of coarse secondary recrystallized grains in the SiC-poor region and fine grains in the SiC-rich regions. A basal plane fiber texture was achieved, with the {0001} plane oriented parallel to the transverse direction (TD). Moreover, grains with their <2-1-10> orientation parallel to the extrusion direction (ED) experienced preferred growth because those grains possessed characteristics such as larger initial size, lower storage energy, and a larger orientation difference from neighboring grains. The SiCp/ZX20K composites extruded at 5mm/s exhibited a yield strength (YS) of 218MPa, with a decent elongation to failure (EL) of 4.8% and an ultimate tensile strength (UTS) of 294MPa which was 2.3 times greater than that of the as-cast state. Increasing the extrusion speed resulted in better overall mechanical properties and reduced the anisotropy in mechanical properties, due to the combined effects of texture, particle orientation and particle distribution.