Characterization of Grain Boundary Deformation Processes in Commercial Purity Titanium Using Nanoindentation and Crystal Plasticity Modeling

Nanguang Su,Guan‐Jun Yang

2014-01-01

Abstract:The nature of plastic deformation across grain boundaries in α-titanium has been studied using instrumented sphero-conical nanoindentation in complement with crystal plasticity modeling. Following crystal orientation mapping using electron backscattered diffraction, indention was preformed (i) in the center of grains to mimic single crystal indentation and (ii) near grain boundaries to carry out bicrystal experiments. The pile-up topography that forms as a function of nanoindentation axis was characterized using atomic force microscopy (AFM). Crystal plasticity fi nite element simulations were carried out iteratively by varying the slip parameters until a best fi t was found between the experimentally measured single crystal pile-up topographies and the simulated single crystal pile-up topographies of several orientations. AFM characterization of bicrystal nanoindents revealed changes in the pileup topographies compared to those for single crystal nanoindents carried out in the same grain. In general, the pile-up topographies were not strongly infl uenced by low angle grain boundaries, indicating signifi cant strain transfer across the boundaries. In contrast, many high angle boundaries strongly infl uenced the pile-up morphology, with changes in the pile-ups noted in both the grain containing the pile-up and in the neighboring grain. The ability to accurately simulate the infl uence of grain boundaries pile-up development was examined by carrying out CPFE simulations of bicrystal nanoindentation. Direct comparison of the AFM-measured topographies with simulated topographies reveals that the general nature of bicrystal pile-up topography is well simulated, but that in general, the measured pile-up transfer is somewhat smaller than the simulated pile-up transfer. The results of the study will be discussed in terms of a number of generalized slip transfer criteria. This research was supported the National Science Foundation through a Materials World Network Grant DMR-1108211 and the complementary Deutsche Forchungsgemeinschaft grant ZA523/3-1.