Abstract:In this paper, we report a facile, "green'', phosphine-free, low-cost, and non-injection method to obtain size-, shape-, and assembly-controllable Cu2-xSe nanocrystals which can be used as uniform building blocks. Different sizes of monodispersed Cu2-xSe nanocrystals were synthesized successfully by simply controlling the reaction temperature. The highly uniform Cu2-xSe nanocrystals can be well controlled from 4 to 20 nm when the temperature was set from 120 to 200 degrees C. By changing the ratios of CuSt(2), oleic acid (OA), oleylamine (OAM), and selenium-octadecene (Se-ODE) precursor, Cu2-xSe nanocrystals with different shapes (hexagonal, elongated hexagonal bipyramid-shaped, trigonal pyramidal-shaped) and assembly behaviors (hexagonal Cu2-xSe nanodiscs with 1D, 2D, and 3D columnar self-assembly, elongated hexagonal bipyramid-shaped Cu2-xSe with 2D and 3D self-assembly, trigonal pyramidal-shaped Cu2-xSe nanocrystals with different arrays) were obtained indeed. Even though both OA and OAM were used as stabilizers to synthesize different shaped Cu2-xSe nanocrystals, FTIR results indicated that the surface of the as-synthesized nanocrystals was only capped by OAM. XRD studies confirmed that three different shapes of Cu2-xSe nanocrystals prepared with this non-injection method are all cubic berzelianite and well-crystallized. Current-voltage (I-V) behaviors of different shaped Cu2-xSe nanocrystals were measured and all found to have low resistivities.

The Size Controlled Synthesis and Self-Assembled of Monodisperse Cu2S Nanocrystals

Phase-Selective Synthesis and Self-Assembly of Monodisperse Copper Sulfide Nanocrystals

Controllable Synthesis of Monodisperse CuS Nanocrystals

Controlled synthesis and self-assembly of highly monodisperse Ag and Ag2S nanocrystals

Controllable Synthesis of Cu<sub>2</sub>S Nanocrystals and Their Assembly into a Superlattice

Size-, Shape-, and Assembly-Controlled Synthesis of Cu2−xSe Nanocrystalsvia a Non-Injection Phosphine-Free Colloidal Method

Colloidal synthesis of monodisperse quaternary CuInSSe nanocrystals

Size Effects In The Oriented-Attachment Growth Process: The Case Of Cu Nanoseeds

Controlled synthesis and characterization of covellite (CuS) nanoflakes

Controlled Synthesis of Luminescent Cuins2 Nanocrystals and Their Optical Properties

Large-Scale Synthesis and Self-Assembly of Monodisperse Hexagon Cu2S Nanoplates

Synthesis of Hierarchical CuS Flower-Like Submicrospheres Via an Ionic Liquid-Assisted Route

Scalable Synthesis of Cu 2 S Double-Superlattice Nanoparticle Systems with Enhanced UV/visible-light-driven Photocatalytic Activity

Size-controlled Preparation of Cu2O Octahedron Nanocrystals and Studies on Their Optical Absorption

Controlled Synthesis, Growth Mechanism, and Properties of Monodisperse CdS Colloidal Spheres.

Large-Scale Synthesis of Single-Crystal Double-Fold Snowflake Cu2s Dendrites

Inorganic Sn-X-Complex-Induced 1d, 2d, and 3d Copper Sulfide Superstructures from Anisotropic Hexagonal Nanoplate Building Blocks

Controllable Synthesis of CuS Nanostructures from Self-Assembled Precursors with Biomolecule Assistance

Facile synthesis and characterization of CuInS2 nanocrystals with different structures and shapes

Synthesis of High-Quality and Self-assembled Cu2ZnSnS4 Nanocrystals

Synthesis of size- and shape-controlled CuO assemblies